| Value | Units | Test Method / Conditions | |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Mold Shrinkage (2.0mm, Parallel) | 1.9 | % | ISO 294-4 |
| Mold Shrinkage (2.0mm, Transverse) | 1.8 | % | ISO 294-4 |
| Water Absorption (24 Hrs) | 1.4 | % | ISO 62 |
| Water Absorption (Equilibrium 50% RH) | 2.7 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Tensile Stregnth at Yield | 82 | MPa | ISO 527 |
| Tensile Stregnth at Break | - | MPa | ISO 527 |
| Elongation at Yield | 4.2 | % | ISO 527 |
| Elongation at Break | 50 | % | ISO 527 |
| Tensile Modulus | 3200 | MPa | ISO 527 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Strength | 95 | MPa | ISO 178 |
| Charpy Notched (23°C) | 5.5 | kJ/m² | ISO 179 |
| Notched lzod (23°C) | 5.4 | kJ/m2 | ISO 180 |
| Value | Units | Test Method / Conditions | |
| Melting Point | 261 | °C | D-3418 |
| HDT (0.45MPa) | 204 | °C | - |
| Coeffiecient of Linear Thermal Expansion (Parallel) | 0.8 x 10-4 | mm ˚C | E-831 |
| Comparative Tracking Index | 600 | Volts | IEC 60112 |
| Volume Resistivity | 4.00E + 14 | ohms/cm | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | IEC 60243 |
| Surface Resistivity | 3.00E + 14 | Ohms | IEC 60093 |