- This is a flexible stiff / creamy polysulphide joint sealant.
- When fully cured, this product is a rubbery elastic sealant with a high mechanical load capacity, good resistance to water, sea water, salt solutions, benzenes, and mineral oils.
- It is root resistant, does not rot, and it has very good retraction properties.
- High mechanical load capacity
- Good chemical resistance
- Resistant against sea water
- Resistant to mineral oils and petroleum
- Suitable for horizontal joints
Applications & Uses
- Markets
- Applications
- Cleaning
Clean tools immediately after use with KÖSTER Universal Cleaner.
- Fields of Application
- This product can be used to permanently and elastically seal horizontal joints in below grade construction, cracks in basements, foundations of buildings, joints in sewage treatment plants, garages, tunnels, etc.
- It is also suited for application on horizontal joints.
- Substrate
- The flanks of the joints have to be clean, solid, and free of grease and dust.
- Substrates must be primed with KÖSTER FS-Primer 2C.
- Application
- Mix both components thoroughly using a slow speed mixer until a homogeneous consistency is reached, (at least 3 minutes).
- The joint is filled approx. 2 hours after priming by pouring or with a caulking gun and is smoothed with a trowel or spatula or straight edge.
- Observe the DIN 18540.
- Consumption
- Approx. 1.6 kg / l void
Joint width (mm) 10 15 20 25 30 35 Thickness of joint sealant (mm) 8 10 12 15 18 20 Deviation allowed (mm) 0 - 2 0 - 2 0 - 2 0 - 6 0 - 6 0 - 8 Distance of joints allowed (m) 2 - 4 2 - 6 4 - 7 5 - 8 6 - 9 7 - 10 Consumption (kg / m) 0.13 0.24 0.38 0.60 0.72 1.12
Properties
- Component A
- Typical Properties
- Component B
- Adhesion and Elongation Capacity
- Modulus of tension at 100% elongation
- At +23°C - min. 0.15 MPA
- At -20°C - max. 0.6 MPA
- Water Impermeability
- Modulus of tension at 100% elongation
- At +23°C - min. 0.15 MPA
- At -20°C - max. 0.6 MPA
- No failure at -20°C - max. 0.6 MPa
- Durability of All Mandated Properties Against Aging
- Change in modulus of tension at 100% elongation max. 10 - 30 %.
Value | Units | Test Method / Conditions | |
Mix Ratio by Weight | 100.0 | — | — |
Value | Units | Test Method / Conditions | |
Adhesion Capacity (No Failure, -20°C) | max. 0.6 | MPA | — |
Resistance to Deflection (Resilience) | min. 70 | % | — |
Resistance to Deflection (Volume Loss) | max. 5 | % | — |
Durability of Water Impermeability Under Chemical Attack | Passed | — | — |
Resistance to Flames | Passed | — | — |
Curing Time (23°C, 50%R.H.) | approx. 24 | hours | — |
Consistency | Stiff / Creamy | — | — |
Density | approx. 1.6 | kg/l | — |
Hardness | approx. 35 | Shore A | — |
Retraction Capacity | min. 80 | % | — |
Total Deformation Permitted | approx. 25 | % | — |
Application Temperature | 5 - 40 | °C | — |
Maximum Application Slope | approx. 15 | % | — |
Value | Units | Test Method / Conditions | |
Mix Ratio by Weight | 13.0 | — | — |
Safety & Health
- Safety
- Wear appropriate Protective Personal Equipment (PPE) when installing the material.
Packaging & Availability
- Packaging
J 231 004 - 4kg combi-package
Storage & Handling
- Pot Life
- approx. 2 hours (20°C, 50%R.H.)
- Storage
- Store the material dry and frost free.
- In originally sealed packages it can be stored for a minimum of 6 months.