Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Provides
- High strength of the coating.
- High impact resistance and elasticity.
- Fast drying.
- High resistance to sunlight and UV radiation.
- Well preserves shine.
Applications & Uses
- Markets
- Recommended Use
Steel surfaces:
- As a single-layer coating in conditions of low and medium atmospheric corrosion categories C2-C3 (ISO-12944-2 / 2018).
- As a top layer (when coating on various types of primers) under the corrosivity categories C2-C4, C5 and CX (ISO-12944-2 / 2018).
- Maintenance coating over old paintedsurfaces.
Non-ferrous and galvanized surfaces:
- As an atmospheric protective coating
Concrete surface:
- In the industry.
- At civil engineering objects.
- Compatible Coatings
Depending on the operating conditions the material can be used with different types of coatings:
- Single pack, moisture cured polyurethane coatings (1 pack PUR) of Rayston.
- Two-component epoxy coatings (2 pack EP) of Rayston.
- Two-component polyurethane coatings (2 pack PUR) of Rayston.
- Surface Preparation
Surface Type Minimum Recommended Surface profile Ry5 (30-75 µm) (ISO 8503-1) Ry5 (30-75 µm) (ISO 8503-1) Primed surfaces & Previously painted surfaces P St2; P Ma
ISO 8501-2,
ISO 12944-4P Sa2; PMa
ISO 8501-2½,
ISO 12944-4Steel surfaces Sa 2 (ISO 8501-1) Sa 2½ (ISO 8501-1) Surfaces of non-ferrous metals and stainless steel Clean with alkaline solution, rinse with water. (SSPC-SP 1) Light surface roughness ISO8501-2, ISO12944-4 Galvanized surfaces Clean with alkaline solution, rinse with water. (SSPC-SP 1) Light surface roughness ISO8501-2, ISO12944-4 Concrete Surfaces SSPC-SP 13 / NACE No. 6 SSPC-SP 13 / NACE No. 6 - Thickness & Theoretical Spreading Rate
Min. Middle Max. Dry Film Thickness 40 μm 70 μm 100 μm Wet Film Thickness 67μm 117 μm 167 μm Spreading Rate 15 m2/l 8.57 m2/l 6 m2/l Note: Practical coverage depends on the application conditions, structure to be painted, roughness of the surface and application method.
- Drying Time
Dry Film Thickness 60µ -5°C 0°C 5°C, 85% RH 10°C, 80% RH 25°C, 50% RH 40°C, 50% RH Dry to touch 3.5 h 3 h 2 h 1 h 45 min 15 min Dry to handle 6 h 5.5 h 5 h 1.5 h 1 h 35 min Min. overcoating interval 16 h 14.5 h 14 h 5 h 2.5 h 1.5 h Full curing 10 d 10 d 8 d 8 d 7 d 5 d Note:
- There is no maximum overcoating interval.
- Rayston Activator may shorter drying time of the coating.
- Dryingand curing time determined at controlled temperatureand relative humidity (RH) 60 - 80%.
- As the relative humidity of the air decreases, the curing time of the coating increases.
- Application Data
Mixing ratio: By volume 4 : 1, By mass 5.2 : 1
Product Volume Resin 4 parts by volume Curing Agent 1 part by volume Stir resin and curing agent separately (slow stirring) and then mix both components thoroughly with propeller stirrer.Before use the temperature of packaging and material should not be less than 3°C higher than the dewpoint. Add thinner only after both components have been thoroughly mixed and stir the mixture.
Thinning: Adding a thinner is not necessary, but if needed Raystonthinner PU may be added up to 10% by volume.
Note: Adding a thinner will increase the drying time. In the case of using thinner other than those recommended, the manufacturer is not responsible for any possible reduction in the quality of thecoating.
Cleaner: Rasytonthinner PU
Pot life (+23 °C): Approx. 1.5 hour after mixing.
- Application Method
Spray Application: Airless spray is the main method of application. For other spraying methods, viscosity correction may be required.
Brush: Application by brush. Recommended for touch-up, stripe coating and small areas.
Roller: Application by roller. Use roller on concrete surfaces.
Properties
- Appearance
- Semi-gloss Coating
- Typical Properties
Value | Units | Test Method / Conditions | |
Solids (By Volume) | 63 - 67 | % | ISO 3233-3 |
Density (А+В) | 1.20 - 1.30 | g/cm³ | ISO 2811-1 |
Volatile Organic Content | 333.0 | g/l | ISO 11890-1 |
Dry Heat Resistance | 120.0 | °C | ASTM D2485 |
Adhesion To Steel | 8.0 | MPa | ISO 4624 |
Air Temperature (Ambient) | - 5 to 45 | °C | - |
Surface Temperature | -5 to 50 | °C | - |
Relative Humidity | max. 85 | % | - |
Dew Point (Lower than Steel Temperature) | min. 3 | °C | - |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety
Use with adequate ventilation. Do not inhale aerosol. Avoid contact with skin. After contact with skin, wash immediately with detergent, soap and water. In case of contact with eyes, rinse immediately with water and seek medical advice immediately
Packaging & Availability
- Packaging
Volume (liters) Size of containers (liters) Comp. A 8 10 Comp. B 2 2.4
Storage & Handling
- Storage & Shelf Life
The product must be stored in original sealed containers. The storage conditions are to keep the containers in a dry, well ventilated space away from source of heat and ignition.
Storage Temperature From 5 to 30°С Component A 24 months Component B 24 months Note: After lasting storage primer shall be stirred thoroughly until its precipitation is spread over the suspension homogeneously. Precipitation in primer does not change its properties or worsen its quality. After the expiration date has passed, it is necessary to check the quality of the paint material.