Larton™ G/40 I6

Identification & Functionality

Chemical Family

Polyphenylene Sulfide (PPS)

Fillers Included

Glass Fiber

Polymer Name

Polyphenylene Sulfide (PPS)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Materials Features

Chemical Resistant,

Low Smoke Emission,

Low Toxicity

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength - at Break (5 mm/min, 23°C)	195	MPa	ISO 527
Tensile Strength - at Break (5 mm/min, 60°C)	180	MPa	ISO 527
Tensile Strength - at Break (5 mm/min, 90°C)	150	MPa	ISO 527
Tensile Strength - at Break (5 mm/min, 120°C)	110	MPa	ISO 527
Tensile Strength - at Break (5 mm/min, 150°C)	85	MPa	ISO 527
Tensile Elongation - at Break (5 mm/min, 23°C)	1.8	%	ISO 527
Tensile Elongation - at Break (5 mm/min, 60°C)	1.7	%	ISO 527
Tensile Elongation - at Break (5 mm/min, 90°C)	2.6	%	ISO 527
Tensile Elongation - at Break (5 mm/min, 120°C)	3	%	ISO 527
Tensile Elongation - at Break (5 mm/min, 150°C)	3.3	%	ISO 527
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C)	15000	MPa	ISO 527
Elastic Modulus Tensile Speed ( 1 mm/min, at 60°C)	14500	MPa	ISO 527
Elastic Modulus Tensile Speed ( 1 mm/min, at 90°C)	14000	MPa	ISO 527
Elastic Modulus Tensile Speed ( 1 mm/min, at 120°C)	9200	MPa	ISO 527
Elastic Modulus Tensile Speed ( 1 mm/min, at 150°C)	6000	MPa	ISO 527
Charpy Unnotched Impact Strength ( +23°C)	40	kJ/m2	ISO 179-1eU
Charpy Notched Impact Strength (+23°C)	10	kJ/m2	ISO 179/1eA

Physical Properties

	Value	Units	Test Method / Conditions
Moisture Absorption (Air, After 24Hrs)	0.04	%	ISO 62-4
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa)	0.20/0.35	%	ISO 294-4
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa))	0.45/0.65	%	ISO 294-4
Density	1.65	g/cm3	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT (0.45 mn/m2)	280	°C	ISO 75
Heat Deflection Temperature - HDT (1.81 mn/m2)	260	°C	ISO 75
Vicat Softening Point - VST (50 N, eating Rate 50°C/H)	260	°C	ISO 306
Coefficient of Linear Thermal Expansion - CLTE (Transversal, +30°C to +100°C)	15	μm/(m·°C)	ISO 11359-2
Coefficient of Linear Thermal Expansion - CLTE - (Longitudinal, +30°C to +100°C)	10	μm/(m·°C)	ISO 11359-2
Continuous Use Temperature - C.U.T (Long Period, 20,000H)	220	°C	ASTM E1641/E1877

Electrical Properties

	Value	Units	Test Method / Conditions
Comparative Tracking Index - CTI (Solution A , Without Surfactant))	125	V	IEC 60112
Surface Resistivity	1.00E+12	ohm	IEC 60093

Flammability

	Value	Units	Test Method / Conditions
Flammability Rating (3.00 mm Thickness)	V-0	-	UL 94
Flammability Rating (1.50 mm Thickness)	V-0	-	UL 94
Flammability Rating (0.75 mm Thickness)	V-0	-	UL 94
Glow Wire Flammability Index - GWFI	960/1	-	IEC60695-2-12
Oxygen Index	44	%	ASTM D 2863

Regulatory & Compliance

Certifications & Compliance

UL 94