Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Tensile Strength - at Break (5 mm/min, 23°C) | 175 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 60°C) | 130 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 90°C) | 105 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 120°C) | 95 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 150°C) | 80 | MPa | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 23°C) | 3.4 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 60°C) | 5.5 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 90°C) | 7.8 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 120°C) | 8.8 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 150°C) | 9.3 | % | ISO 527 |
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C) | 8200 | MPa | ISO 527 |
Elastic Modulus Tensile Speed ( 1 mm/min, at 60°C) | 6000 | MPa | ISO 527 |
Elastic Modulus Tensile Speed ( 1 mm/min, at 90°C) | 4400 | MPa | ISO 527 |
Elastic Modulus Tensile Speed ( 1 mm/min, at 120°C) | 3900 | MPa | ISO 527 |
Elastic Modulus Tensile Speed ( 1 mm/min, at 150°C) | 3400 | MPa | ISO 527 |
Charpy Unnotched Impact Strength ( +23°C) | 90 | kJ/m2 | ISO 179-1eU |
Charpy Notched Impact Strength (+23°C) | 12 | kJ/m2 | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Moisture Absorption (Air, After 24Hrs) | 0.27 | % | ISO 62-4 |
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa) | 0.35/0.65 | % | ISO 294-4 |
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa)) | 0.75/1.05 | % | ISO 294-4 |
Dimensional stability | 45 | - | -- |
Density | 1.36 | g/cm3 | ISO 1183/A |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (0.45 mn/m2) | 260 | °C | ISO 75 |
Heat Deflection Temperature - HDT (1.81 mn/m2) | 245 | °C | ISO 75 |
Vicat Softening Point - VST (50 N, eating Rate 50°C/H) | 255 | °C | ISO 306 |
Coefficient of Linear Thermal Expansion - CLTE - (Longitudinal, +30°C to +100°C) | 45 | μm/(m·°C) | ISO 11359-2 |
Continuous Use Temperature - C.U.T (Long Period, 20,000H) | 130 | °C | ASTM E1641/E1877 |
Value | Units | Test Method / Conditions | |
Surface Resistivity | 1.00E+12 | ohm | IEC 60093 |