Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
Value | Units | Test Method / Conditions | |
Tensile Strength - at Yield (5 mm/min, 23°C) | 55 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 23°C) | 55 | MPa | ISO 527 |
Tensile Elongation - at Yield (5 mm/min, 23°C) | 5 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 23°C) | 12 | % | ISO 527 |
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C) | 2800 | MPa | ISO 527 |
Charpy Unnotched Impact Strength ( +23°C) | No Break | - | ISO 179-1eU |
Charpy Notched Impact Strength (+23°C) | 6 | kJ/m2 | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa) | 0.60/1.00 | % | ISO 294-4 |
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa)) | 0.60/1.00 | % | ISO 294-4 |
Density | 1.36 | g/cm3 | ISO 1183/A |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (0.45 mn/m2) | 250 | °C | ISO 75 |
Heat Deflection Temperature - HDT (1.81 mn/m2) | 230 | °C | ISO 75 |
Vicat Softening Point - VST (50 N, eating Rate 50°C/H) | 250 | °C | ISO 306 |
Coefficient of Linear Thermal Expansion - CLTE - (Longitudinal, +30°C to +100°C) | 150 | μm/(m·°C) | ISO 11359-2 |