Latamid™ 66 S/30

Identification & Functionality

Chemical Family

Polyamides

Fillers Included

Glass Bead

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Chemical Resistant,

Dimensional Stability,

Fatigue Resistant,

Good Colorability,

Good Electrical Properties,

Good Mechanical Properties,

Good Stiffness,

Good Thermal Stability,

High Flow,

High Gloss,

Impact Resistance,

Low Shrinkage,

UV Resistant

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Exterior & Body,

Interior,

Other Automotive Applications

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Other Devices & Assemblies

Electrical & Electronics — Parts & Components

Other Parts & Components

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Exterior Parts,

Automotive Interior Parts,

Computer Components,

Electrical/Electronic Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength - at Yield (5 mm/min, 23°C)	-	-	ISO 527
Tensile Strength - at Yield (5 mm/min, 60°C)	60	MPa	ISO 527
Tensile Strength - at Yield (5 mm/min, 90°C)	40	MPa	ISO 527
Tensile Strength - at Yield (5 mm/min, 120°C)	30	MPa	ISO 527
Tensile Elongation - at Break (5 mm/min, 23°C)	5	%	ISO 527
Tensile Elongation - at Yield (5 mm/min, 60°C)	10	%	ISO 527
Tensile Elongation - at Yield (5 mm/min, 90°C)	14	%	ISO 527
Tensile Elongation - at Yield (5 mm/min, 120°C)	15	%	ISO 527
Tensile Elongation - at Yield (5 mm/min, 150°C)	16	%	ISO 527
Tensile Elongation - at Break (5 mm/min, 60°C)	15	%	ISO 527
Tensile Elongation - at Break (5 mm/min, 90°C)	20	%	ISO 527
Tensile Elongation - at Break (5 mm/min, 120°C)	25	%	ISO 527
Tensile Elongation - at Break (5 mm/min, 150°C)	45	%	ISO 527
Tensile Elongation - at Yield (5 mm/min, 23°C)	-	-	ISO 527
Charpy Unnotched Impact Strength ( -20°C)	15	kJ/m2	ISO 179-1eU
Charpy Unnotched Impact Strength ( +23°C)	20	kJ/m2	ISO 179-1eU
Charpy Notched Impact Strength (+23°C)	2	kJ/m2	ISO 179/1eA
Charpy Notched Impact Strength (-20°C)	0.8	kJ/m2	ISO 179-1eA

Physical Properties

	Value	Units	Test Method / Conditions
Moisture Absorption (Air, After 24Hrs)	0.27	%	ISO 62-4
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa)	0.90/1.20	%	ISO 294-4
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa))	0.90/1.20	%	ISO 294-4
Dimensional stability	70	-	--
Density	1.34	g/cm3	ISO 1183/A

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT (1.81 mn/m2)	140	°C	ISO 75
Heat Deflection Temperature - HDT (0.45 mn/m2)	230	°C	ISO 75
Vicat Softening Point - VST (50 N, eating Rate 50°C/H)	225	°C	ISO 306
Coefficient of Linear Thermal Expansion - CLTE - (Longitudinal, +30°C to +100°C)	95	μm/(m·°C)	ISO 11359-2
Continuous Use Temperature - C.U.T (Long Period, 20,000H)	90	°C	ASTM E1641/E1877

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity	1.00E+12	ohm	IEC 60093

Packaging & Availability

Country Availability

Brazil,

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Asia Pacific
• Europe
• Latin America
• North America