Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength - at Break (5 mm/min, 23°C) | 210 | MPa | ISO 527 |
| Tensile Strength - at Break (5 mm/min, 60°C) | 195 | MPa | ISO 527 |
| Tensile Strength - at Break (5 mm/min, 90°C) | 175 | MPa | ISO 527 |
| Tensile Strength - at Break (5 mm/min, 120°C) | 125 | MPa | ISO 527 |
| Tensile Strength - at Break (5 mm/min, 150°C) | 65 | MPa | ISO 527 |
| Tensile Elongation - at Break (5 mm/min, 150°C) | 8 | % | ISO 527 |
| Tensile Elongation - at Break (5 mm/min, 120°C) | 4 | % | ISO 527 |
| Tensile Elongation - at Break (5 mm/min, 23°C) | 1.9 | % | ISO 527 |
| Tensile Elongation - at Break (5 mm/min, 60°C) | 2.1 | % | ISO 527 |
| Tensile Elongation - at Break (5 mm/min, 90°C) | 2.3 | % | ISO 527 |
| Elastic Modulus Tensile Speed ( 1 mm/min, at 60°C) | 13000 | MPa | ISO 527 |
| Elastic Modulus (Tensile Speed - 1 mm/min, 23°C) | 14500 | MPa | ISO 527 |
| Elastic Modulus Tensile Speed ( 1 mm/min, at 90°C) | 11500 | MPa | ISO 527 |
| Elastic Modulus Tensile Speed ( 1 mm/min, at 120°C) | 9000 | MPa | ISO 527 |
| Elastic Modulus Tensile Speed ( 1 mm/min, at 150°C) | 4000 | MPa | ISO 527 |
| Charpy Unnotched Impact Strength ( +23°C) | 60 | kJ/m2 | ISO 179-1eU |
| Charpy Notched Impact Strength (+23°C) | 8.5 | kJ/m2 | ISO 179/1eA |
| Value | Units | Test Method / Conditions | |
| Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa) | 0.25/0.45 | % | ISO 294-4 |
| Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa)) | 0.45/0.70 | % | ISO 294-4 |
| Density | 1.53 | g/cm3 | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (0.45 mn/m2) | 290 | °C | ISO 75 |
| Heat Deflection Temperature - HDT (1.81 mn/m2) | 265 | °C | ISO 75 |
| Vicat Softening Point - VST (50 N, eating Rate 50°C/H) | 260 | °C | ISO 306 |
| Continuous Use Temperature - C.U.T (Long Period, 20,000H) | 145 | °C | ASTM E1641/E1877 |
| Coefficient of Linear Thermal Expansion - CLTE - (Longitudinal, +30°C to +100°C) | 15 | μm/(m·°C) | ISO 11359-2 |
| Value | Units | Test Method / Conditions | |
| Surface Resistivity | 1.00E+12 | ohm | IEC 60093 |