Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Tensile Strength - at Break (5 mm/min, 23°C) | 40 | MPa | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 23°C) | 0.8 | % | ISO 527 |
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C) | 8900 | MPa | ISO 527 |
Charpy Unnotched Impact Strength ( +23°C) | 10 | kJ/m2 | ISO 179-1eU |
Charpy Notched Impact Strength (+23°C) | 7 | kJ/m2 | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa) | 0.50/0.90 | % | ISO 294-4 |
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa)) | 0.50/0.90 | % | ISO 294-4 |
Density | 10.85 | g/cm3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (0.45 mn/m2) | 160 | °C | ISO 75 |
Heat Deflection Temperature - HDT (1.81 mn/m2) | 105 | °C | ISO 75 |
Vicat Softening Point - VST (50 N, eating Rate 50°C/H) | 165 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Electromagnetic Reflection (Bekiscan - Cp) | 95 | % | -- |
Surface Resistivity | 100.0 | ohm | ASTM D 257 |
Volume Resistivity | 1000.0 | ohm.cm | ASTM D 257 |