Value | Units | Test Method / Conditions | |
Tensile Strength - at Break (5 mm/min, 23°C) | 115 | MPa | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 23°C) | 1.5 | % | ISO 527 |
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C) | 11000 | MPa | ISO 527 |
Friction Coefficient - Static | 0.24 | - | ASTM D 1894 |
Friction Coefficient - Dynamic | 0.22 | - | ASTM D 1894 |
Charpy Unnotched Impact Strength ( +23°C) | 20 | kJ/m2 | ISO 179-1eU |
Charpy Notched Impact Strength (+23°C) | 6.5 | kJ/m2 | ISO 179/1eA |
Wear Factor | 8× 10^-7 | mm3/(Nm) | ASTM D 3702 |
Value | Units | Test Method / Conditions | |
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa) | 0.50/0.80 | % | ISO 294-4 |
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa)) | 1.20/1.60 | % | ISO 294-4 |
Density | 1.54 | g/cm3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (0.45 mn/m2) | 295 | °C | ISO 75 |
Heat Deflection Temperature - HDT (1.81 mn/m2) | 275 | °C | ISO 75 |
Vicat Softening Point - VST (50 N, eating Rate 50°C/H) | 245 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Surface Resistivity | 1.00E+12 | ohm | IEC 60093 |