Latimass™ 52/11-01 D020

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Other Filler

Polymer Name

Polypropylene Homopolymer (HPP)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Homopolymer

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength - at Break (5 mm/min, 23°C)	15	MPa	ISO 527
Tensile Elongation - at Break (5 mm/min, 23°C)	1	%	ISO 527
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C)	2900	MPa	ISO 527
Charpy Unnotched Impact Strength ( +23°C)	10	kJ/m2	ISO 179-1eU
Charpy Notched Impact Strength (+23°C)	1.3	kJ/m2	ISO 179-1eA

Physical Properties

	Value	Units	Test Method / Conditions
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa)	1.20/1.50	%	ISO 294-4
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa))	1.25/1.55	%	ISO 294-4
Density	2.05	g/cm3	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT (0.45 mn/m2)	95	°C	ISO 75
Heat Deflection Temperature - HDT (1.81 mn/m2)	65	°C	ISO 75
Vicat Softening Point - VST (50 N, eating Rate 50°C/H)	95	°C	ISO 306

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity	1.00E+12	ohm	IEC 60093