Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Tensile Strength - at Break (5 mm/min, 23°C) | 15 | MPa | ISO 527 |
Tensile Strength - at Yield (5 mm/min, 23°C) | 15 | MPa | ISO 527 |
Tensile Elongation - at Yield (5 mm/min, 23°C) | 4 | % | ISO 527 |
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C) | 2200 | MPa | ISO 527 |
Charpy Unnotched Impact Strength ( +23°C) | 20 | kJ/m2 | ISO 179-1eU |
Charpy Notched Impact Strength (+23°C) | 1.3 | kJ/m2 | ISO 179-1eA |
Tensile Elongation at Break (5 mm/min, 23°C) | min. 100.0 | - | ISO 527 |
Value | Units | Test Method / Conditions | |
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa) | 1.05/1.35 | % | ISO 294-4 |
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa)) | 1.00/1.30 | % | ISO 294-4 |
Density | 0.9 | g/cm3 | ASTM D1505 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (0.45 mn/m2) | 100 | °C | ISO 75 |
Heat Deflection Temperature - HDT (1.81 mn/m2) | 60 | °C | ISO 75 |
Vicat Softening Point - VST (50 N, eating Rate 50°C/H) | 100 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Surface Resistivity | 1.00E+12 | ohm | IEC 60093 |