| Value | Units | Test Method / Conditions | |
| Tensile Strength - at Yield (5 mm/min, 23°C) | 35 | MPa | ISO 527 |
| Tensile Strength - at Break (5 mm/min, 23°C) | 30 | MPa | ISO 527 |
| Tensile Elongation - at Yield (5 mm/min, 23°C) | 4 | % | ISO 527 |
| Tensile Elongation - at Yield (5 mm/min, 60°C) | - | - | ISO 527 |
| Tensile Elongation - at Yield (5 mm/min, 90°C) | - | - | ISO 527 |
| Tensile Elongation - at Yield (5 mm/min, 120°C) | - | - | ISO 527 |
| Elastic Modulus (Tensile Speed - 1 mm/min, 23°C) | 2200 | MPa | ISO 527 |
| Charpy Unnotched Impact Strength ( +23°C) | 30 | kJ/m2 | ISO 179-1eU |
| Charpy Notched Impact Strength (+23°C) | 3.5 | kJ/m2 | ISO 179-1eA |
| Tensile Elongation at Break (5 mm/min, 23°C) | min. 100.0 | — | ISO 527 |
| Value | Units | Test Method / Conditions | |
| Moisture Absorption (Air, After 24Hrs) | 0.07 | % | ISO 62-4 |
| Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa) | 1.70/2.00 | % | ISO 294-4 |
| Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa)) | 1.70/2.00 | % | ISO 294-4 |
| Dimensional stability | 58 | - | -- |
| Density | 1.42 | g/cm3 | STANDARD ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (1.81 mn/m2) | 65 | °C | ISO 75 |
| Heat Deflection Temperature - HDT (0.45 mn/m2) | 165 | °C | ISO 75 |
| Vicat Softening Point - VST (50 N, eating Rate 50°C/H) | 180 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Electromagnetic Reflection (Bekiscan - Cp) | 94 | % | -- |
| Surface Resistivity | 100.0 | ohm | ASTM D 257 |
| Volume Resistivity | 1000.0 | ohm.cm | ASTM D 257 |