Latistat™ 73/13-06

Identification & Functionality

Polymer Name

Polyacetal Copolymer (POM)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyacetals

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength - at Break (5 mm/min, 23°C)	55	MPa	ISO 527
Tensile Elongation - at Break (5 mm/min, 23°C)	5	%	ISO 527
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C)	3000	MPa	ISO 527
Charpy Unnotched Impact Strength ( +23°C)	35	kJ/m2	ISO 179-1eU
Charpy Notched Impact Strength (+23°C)	5	kJ/m2	ISO 179/1eA

Physical Properties

	Value	Units	Test Method / Conditions
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa)	2.00/2.30	%	ISO 294-4
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa))	2.05/2.25	%	ISO 294-4
Density	1.4	g/cm3	ASTM D1505

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT (0.45 mn/m2)	135	°C	ISO 75
Heat Deflection Temperature - HDT (1.81 mn/m2)	85	°C	ISO 75
Vicat Softening Point - VST (50 N, eating Rate 50°C/H)	150	°C	ISO 306

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity	1.00E+05	ohm	Interal Method