- Ready-to-Use Product Features
- Advantages
- UV resistant
- Multi-purpose, self-leveling epoxy
- High gloss finish
- Improved leveling and working properties
- Excellent durability and wear resistance
- Acceptable for use in broadcast systems
- May be used to create a trowel down mortar
- Clear epoxy base can be tinted with SPARTACOTE
- Universal Pigments
Applications & Uses
- Markets
- Compatible Substrates & Surfaces
- Uses
- Healthcare facilities
- Educational facilities
- Single & multi-family residential
- Retail spaces
- Manufacturing plants
- Food & Beverage manufacturing
- Stadium & event spaces
- Pharmaceutical & research facilities
- Laboratories & clean rooms
- Commercial/Institutional kitchens
- Suitable Substrates
- Concrete
- Tile
- SPARTACOTE Epoxy Floor Systems
- SPARTACOTE Urethane Cement Systems
- Installation
Approximate Coverage
SPARTACOTE Surface Build UV may be applied between 10.0 mils (0.25 mm) and 20 mils (0.50mm) WFT.
WFT DFT Coverage 10.0 mils (0.25 mm) 9.9 mils (0.25 mm) 160 ft2/gal (3.9 m2/L)
15.0 mils (0.38 mm) 14.9 mils (0.38 mm) 107 ft2/gal (2.6 m2/L)
20.0 mils (0.50 mm) 19.8 mils (0.50 mm) 80 ft2/gal (2.0 m2/L)
It is recommended to prime all surfaces to be coated prior to application of SPARTACOTE Surface Build UV. The use of a primer will increase adhesion to the substrate and reduce the occurrence of fisheyes, blistering, pinholes & outgassing. Ensure that proper recoat windows are observed. See applicable primer technical data sheet for surface preparation requirements.
Compatible SPARTACOTE Primers:
- SPARTACOTE General Primer (DS 622.6)
- SPARTACOTE WB Epoxy Primer (DS 085.8)
- LATICRETE® VAPOR BAN™ ER (DS 35216.0)
- SPARTACOTE Moisture Vapor Barrier (DS 087.5)
Surface Preparation - Concrete
Surfaces to be coated must be free of grease and any other contaminants that may impede adhesion. Always check the surface for any bond inhibitors prior to application. Any repairs must be addressed prior to application and should be repaired in accordance with ICRI standards. Substrate defects (voids, bugholes, divots, etc.) should be filled smooth with surrounding substrate surface utilizing either SPARTACOTE Fast Fix or SPARTACOTE Epoxy Fill Coat prior to the application of SPARTACOTE Surface Build UV.
Concrete must be mechanically profiled to an ICRI CSP3 to 5. Ensure that all surface laitance is removed prior to coating. The prepared surface should have a tensile pulloff strength of 200 psi (1.4 MPa) or greater when tested in accordance with ASTM C1583. If wet grinding, surface must be allowed to completely dry prior to coating. Concrete must be tested for moisture prior to installation of any coatings. The relative humidity (RH) of the slab must not exceed 75% as tested per ASTM f²170 or >3lbs/1000sqft/24hr per ASTM F1869. If moisture in the slab exceeds these limits, the use of LATICRETE VAPOR BAN ER or SPARTACOTE Moisture Vapor Barrier is required prior to installing SPARTACOTE Surface Build UV.
Mixing
SPARTACOTE Surface Build UV is mixed at a ratio of 3A:2B by volume. Prior to mixing, stir individual components to disperse any materials that may have settled.
If tinting with SPARTACOTE Universal Pigments, mix pigments into the Part A prior to combining Parts A and B at a loading rate of 1 small unit per mixed gallon of resin (A+B) or 1 large unit per 5 gallons of mixed resin (A+B). Add full contents of SPARTACOTE Universal Pigment unit directly into Part A. Scrape sides and ensure all pigment is removed from the jar. Mix pigment into Part A with a slow speed drill mixer to fully disperse the pigments until a uniform color and consistency is achieved, approximately 2 minutes. SPARTACOTE Universal Pigments are intended to be added in addition to the existing resin and will not adversely affect the base resin physical properties or mix ratio. No resin should be removed.
Combine 3 parts A to 2 parts B. Mix for 2-3 minutes with a slow speed drill until a uniform consistency and appearance is achieved. Immediately after mixing apply product to properly prepared and primed substrate.
Application
SPARTACOTE Surface Build UV can be applied by brush, roller and/or notched squeegee. Suggestedapplication thickness is 15 mils WFT (0.38 mm) mm or a spread rate of 107 ft2 /gal (2.5 m² /L). Spread evenly over all primed surfaces and immediately backroll with a 3/8" nap non-shedding roller. A spiked roller may also be utilized to deaerate and help level. For broadcast systems, immediately following the backroll and while the material is still wet broadcast media with either a mechanical sprayer or by hand in a “rainfall pattern” into the wet resin to refusal or rejection.
To optimize intercoat adhesion, appropriate recoat times must be observed. Exposure of the coating to direct sunlight will considerably shorten the recoat times. If recommended recoat times are exceeded, consult a LATICRETE Technical Service Representative; sanding or abrasive blasting may be required. With all epoxies after priming and before each additional coat, examine the surface for amine blush (oily film). If present, remove by cleaning the surface with acetone.
Mixing (Trowel Down Mortar)
SPARTACOTE Surface Build UV may be mixed with aggregate to create a trowel down mortar.
Important : Priming of the substrate is required prior to applying epoxy mortar to the ensure substrate adhesion.
For mixing trowel down mortar, it is recommended to us a concrete mixer. Begin by combining 77 fl.oz. Part A with 51 fl.oz Part B and mixing until a uniform color and consistency is achieved. Slowly add 60 lbs of SPARTACOTE Blended Quartz aggregate, mixing continuously until all material is wetted and a uniform consistency mortar is achieved. Apply mixed mortar directly onto the primed concrete.
Application (Trowel Down Mortar)
SPARTACOTE Surface Build UV trowel down mortar should be spread evenly over the floor with a gage rake or trowel to desired thickness. Suggested application thickness is 3/16" - 1/4" (4.8-6.4 mm). Finish with a power trowel (plastic blade for protection) or finishing trowel. Coverage rates will vary depending on surface profile application thickness and degree of compaction during troweling.
To optimize intercoat adhesion, appropriate re-coat times must be observed. Exposure of the coating to direct sunlight will considerably shorten the re-coat times. If recommended recoat times are exceeded, consult a LATICRETE Technical Service Representative; sanding or abrasive blasting may be required.With all epoxies after priming and before each additional coat, examine the surface for amine blush (oily film). If present, remove by cleaning the surface with acetone.
Notes
Mock-ups and field test areas are required in order to validate performance and appearance related characteristics (including but not limited to color, inherent surface variations, wear, anti dusting, abrasion resistance, chemical resistance, stain resistance, coefficient of friction, etc.) to ensure system performance as specified for the intended use, and to determine approval of the coating system. Variability in job site conditions (including but not limited to surface preparation, sunlight, humidity, dew point, temperature, etc.) during application of SPARTACOTE products may lead to fisheyes, blistering, pinholes, wrinkling, or outgassing of air in the concrete and are not product defects. Double priming, shading or evening application may be required.
Cleaning
Use acetone or xylene to clean tools and equipment.- Maintenance
The long-term performance, appearance, and life expectancy of wear surface products are critically dependent upon a good routine maintenance program designed specifically for the installed wear surface. SPARTACOTE floor coating systems are nonporous, causing dirt and contaminants to remain on the surface. The use of properly placed walk-off mats, inside and outside, will help increase the life of the floor. Recommend maintenance program consist of frequent and thorough cleaning utilizing a neutral pH cleaner. The frequency of washing will vary depending on floor usage type, traffic, and age.
Properties
- Working Properties
- Physical Properties
- Typical Properties
- Note
Working properties based on 70°F (21°C) and 50% RH. Changes in ambient conditions may cause times to vary.
| Value | Units | Test Method / Conditions | |
| Solids (by Volume) | 99.0 | % | — |
| Mix Ratio (by Volume) | 99.0 | % | — |
| Mix Ratio (A:B) | 3 : 2 | — | — |
| Recoat Time | max. 12 | hours | — |
| Recoat Time | min. 60 | minutes | — |
| Foot Traffic | 5.0 | days | — |
| Vehicular Traffic | 24.0 | hours | — |
| Full Cure | 48.0 | hours | — |
| Value | Units | Test Method / Conditions | |
| Adhesion (Concrete Failure) | min. 300 (min. 2.1) | psi(MPa) | ASTM D7234 |
| Tensile Bond Strength | 2,350 (16.2) | psi(MPa) | ASTM D2370 |
| Hardness | 75.0 | Shore D | ASTM D2240 |
| Abrasion Strength (Loss) | 12.0 | mg | ASTM D4060 |
| Impact Resistance | 135 (183) | in-lb(Nm) | ASTM D5420 |
| Mandrel Bend (4 mm) | Pass | — | ASTM D522 |
| Gloss 60 Degree | min. 90 | gu | — |
| Value | Units | Test Method / Conditions | |
| VOC/LEED (as intended for use) | 19.0 | g/L | — |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Cautions
- Wear protective gloves, clothing and eye protection.
- Causes severe skin burns. If skin irritation or rash occurs: get medical advice/attention.
- Causes serious eye damage. If in eyes: Rinse cautiously with water for several minutes. Remove contact lenses if present and easy to do. Call a physician immediately.
- Harmful if swallowed. Rinse mouth do not induce vomiting. Call a physician immediately.
- Keep out of reach of children.
Packaging & Availability
- Packaging
SPARTACOTE Surface Build UV is mixed at 3A:2B by volume.
- Part A: 9852-0005-A 3.0 gal (11.4L) in a 6 gal (22.7) pail
- Part B: 9852-0005-B 2.0 gal (7.6L) in a 3.5 gal (13.2L) pail
Storage & Handling
- Shelf LIfe
Factory sealed containers of this product are guaranteed to be of first quality for two (2) years.
Limitations
- Substrate temperature must be between 50ºF (10ºC) and 90ºF (32ºC)
- Ambient relative humidity must not exceed 90%
- Substrate temperature must be 5ºF (3ºC) above dew point
- Product is intended for interior applications only