Products

On the basis of the activated anionic reaction LiNNOTAMHiPERFORMANCE 1200 Manufactured using the pressureless free-standing casting process. The process creates a high-molecular, highly crystalline and largely stressfree material with very good Wear resistance and dimensional stability

LiNNOTAM with oil finely distributed in the material. LiNNOTAMGLiDE has the added Lubricant self-lubricating properties and has excellent wear resistance low coefficient of friction.

Compared to unreinforced PA 6.6, the Glass fibers improved tensile / compressive strength, Rigidity and dimensional stability as well as a lower one Water absorption reached. For sliding applications is closed note that the sliding partner through the fiberglass can be attacked

Polyamide 12 produced by extrusion with good strength, very good impact strength, good Damping behavior as well as high chemical Resistance. Because of its low tendency to Particularly dimensionally stable moisture absorption.

The properties are essentially the same as those of LiNNOTAM comparable. By adding molybdenum disulphite, a higher crystallinity is achieved in the material compared to pure cast polyamide.

The properties are essentially comparable to those of LiNNOTAM. By using a stabilizer, the thermal-oxidative Counteracted material degradation when exposed to temperature. In comparison to pure cast polyamide, higher usage temperatures can be achieved realize.

Extruded polyamide 6 with good strength, impact resistance and good damping properties behave. Due to the manufacturing process, PA 6 has a higher moisture absorption. Compared to cast polyamide, however, it is less dimensionally stable & wear-resistant.

LiNNOTAM with solid lubricants, additives and stabilizers finely distributed in the material. LiNNOTAMGLIDE Pro T has self-lubricating properties due to the added components and shows excellent wear resistance at very high low coefficient of friction.

In essence, the properties are similar to those of LiNNOTAM comparable. Through the use of special Additives is compared to pure cast polyamide however, a higher crystallinity is achieved in the material.

Polyamide produced on the basis of direct polymerisation in casting molds with a partially crystalline structure. The high proportion of crystallites leads to excellent mechanical properties such as very high abrasion and wear resistance, hardness and rigidity.

Compared to LiNNOTAM indicates LiNNOTAMDRiVE 600 Fe higher impact and shock resistance, higher elasticity and less tendency to absorb moisture. In addition, the material is characterized by a improved creep behavior.

This polyamide from caprolactam and laurolactam produced in the free-casting process shows in comparison to pure LiNNOTAM has a higher impact and shock resistance as well as a lower tendency to absorb moisture. In addition, the material is characterized by improved creep behavior and higher elasticity.

Polyamide produced in the extrusion process with high hardness, rigidity and wear resistance but lower impact strength. The properties of PA66 are comparable to those of PA6 G. the However, the material absorbs and is more moisture less true to size.