Hot polymerized SBR 1009 is recommended for use in calendared products such as slab soling for footwear, and in extruded mechanical goods where smoothness and controlled shrinkage are critical requirements. It is also widely used in sealants and adhesives.

SBR 1763 is an environmentally friendly version of SBR 1721 replacing aromatic extender oil with 37.5 parts of low Polycyclic Aromatic Hydrocarbon naphthenic oil. It was developed for tire applications.

SBR 1605 is a carbon black master batch (CBMB) SBR with 50 parts of N-550 carbon black.

SBR 1507 offers the lowest Mooney viscosity of all SBR 1502 type elastomers. It is a light-colored, general purpose, cold SBR elastomer. It enables a maximum filler loading in rubber applications.

Duradene™711 is a solution polymerized non-oil extended styrene-butadiene rubber copolymer. It contains 18.0% bound styrene and a non-volatile antioxidant stabilizer system. Duradene™711 offers excellent abrasion resistance and low temperature performance. It is often used in tire formulas with low black and oil loadings where good wear and hysteresis are desired.

Hot polymerized SBR 1009AF is used in spray applied adhesives, calendared products, and extruded mechanical goods where smoothness and controlled shrinkage are critical requirements.

Hot polymerized SBR 1011AC elastomer is recommended for adhesive and pressure sensitive tape and label applications, and in mechanical rubber goods where non-staining and high tack is essential.

Hot polymerized SBR 1009AFC is recommended for use in aerosol spray adhesives, mastics, sealants and other general purpose adhesive applications requiring low shrinkage, sag resistance, sprayability or trowelability.

SBR 4684 is a developmental carbon black master batch (CBMB) containing 52 parts of N-234 carbon black. It is extended with 10 parts of highly aromatic oil. SBR 4684 has excellent abrasion resistance, superior physical properties and is smooth processing. Product is made to order on demand.

Hot polymerized SBR 1006 elastomer is used in applications such as adhesives, mechanical rubber goods, floor tile, cove base and brake friction products.

Hot polymerized SBR 1012C elastomer is particularly useful as a binder for fibrous materials. It imparts increased cohesive strength when added to an adhesive mixture.

SBR 1778 is a general-purpose cold polymerized, naphthenic oil-extended elastomer. It exhibits excellent UV light stability for a SBR polymer.

SBR 1502 is a light-colored, general purpose cold SBR elastomer It provides the maximum in physical properties along with excellent color characteristics.

SBR 1783L is an environmentally friendly version of SBR 1712 replacing aromatic extender oil with a non-hazardous RAE oil. It was developed for tire applications.

Duradene™706 is a solution polymerized non-oil extended styrene-butadiene rubber copolymer. It contains 23.5% bound styrene and has a non-volatile antioxidant stabilizer system. Duradene™706 offers very good abrasion resistance and low hysteresis properties. It can also be used as a replacement for emulsion SBR 1502 in most rubber applications.

SBR 1888 is a carbon black master batch (CBMB) based on SBR 1712 latex and 82.5 parts N-339 carbon black similar to SBR 1848 but extended with low PCA RAE extender oil. It provides tensile properties greater than equivalent CBMB produced with HAF or HAF-H carbon black, and superior abrasion resistance.

SBR 1783 is an environmentally friendly version of SBR 1712 replacing aromatic extender oil with a 37.5 parts of low Polycyclic Aromatic Hydrocarbon RAE oil. It was developed for tire applications.

SBR 1769 is an environmentally friendly version of SBR 1721 with the highest bound styrene content, and a naphthenic oil extender oil. It was developed for tire applications.

SBR 1732N is an environmentally friendly version of SBR 1721 with higher bound styrene content, and aromatic extender oil replaced with a naphthenic oil. It was developed for tire applications.

Hot polymerized SBR 4503C is used in construction mastics, adhesives and sealants intended for installing panels, furring strips, wood molding, plywood or hardboard. It offers a strong and instant bond that retains precise placement. It exhibits excellent shear strength and yields a stiffer film when used in tape, PSA or label application.

Hot polymerized SBR 1011AE elastomer is recommended for adhesives, pressure sensitive tape and label, and mechanical rubber goods applications where nonstaining and high tack is essential.

SBR 1502L is a lower viscosity version of SBR 1502. It is a light-colored, general purpose cold SBR elastomer which provides the maximum in physical properties along with excellent color characteristics.

SBR 1712L is a general-purpose cold polymerized elastomer extended with 37.5 parts of highly aromatic oil. It is a low Mooney viscosity version of SBR 1712. It has excellent processing properties and superior polymer stability.

SBR 1789 is an environmentally friendly version of SBR 1712 replacing aromatic extender oil with a non-hazardous RAE oil. SBR 1789 contains a higher level of bound styrene. It was developed for tire applications.

Hot polymerized SBR 1006C elastomer is used in applications such as adhesives, mechanical rubber goods, floor tile, cove base and brake friction products.

Hot polymerized SBR 1013 elastomer is used in adhesives, tire liners, and mechanical rubber goods, including auto mounts and household products.

SBR 1686 is a carbon black master batch (CBMB) based on SBR 1500 latex and N-330 carbon black. It has a low level of oil extension and provides high tensile properties.

SBR 1500 is a general-purpose cold SBR with higher physicals and abrasion resistance than hot polymerized equivalents. It processes readily, provides the highest tensile strength available in cold SBR polymers, and is suitable for products which do not require resistance to staining and discoloration.

SBR 1712 is a general-purpose cold polymerized elastomer extended with 37.5 parts of highly aromatic oil. It has excellent processing properties and superior polymer stability.

Hot polymerized SBR 1009C is recommended for use in calendared products and extruded mechanical goods. It is also widely used in sealants and adhesives.

Hot polymerized SBR 1012 elastomer is particularly useful as a binder for fibrous materials. It imparts increased cohesive strength when added to an adhesive mixture.