Features & Benefits
- Materials Features
- Key Benefits
- High rigidity
- High strength
- Low odor
- Good chemical resistance
- Extremely low shrinkage
- Nano reinforced
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Composite-X Use Cases
Liqcreate Composite-X has features like excellent chemical resistance, high strength and high stiffness which makes it ideal for wind tunnel testing, fluid flow components, automotive and heavy duty industrial applications.
Properties
- Physical Form
- Appearance
- Opaque white liquid
- Mechanical Properties
- Typical Properties
- Note
*Parts were post-cured in a Wicked Engineering Curebox for 60 minutes at 60°C prior to testing. Thermally cured parts were cured for 2 hours at 100°C in a conventional oven after being UV-curing. These values may vary and depend on individual machine processing and post-curing.
| Value | Units | Test Method / Conditions | |
| Tensile Strength (60 minutes UV Curing, at 60°C) | 50 - 75 | MPa | ASTM D638 |
| Tensile Modulus (60 minutes UV Curing, at 60°C) | 7.5 - 8.5 | GPa | ASTM D638 |
| Elongation at Break (60 minutes UV Curing, at 60°C) | 1.0 | % | ASTM D638 |
| Flexural Strength (60 minutes UV Curing, at 60°C) | 140 - 150 | MPa | ASTM D790 |
| Flexural Modulus (60 minutes UV Curing, at 60°C) | 7.5 - 8.5 | GPa | ASTM D790 |
| Notched Izod Impact (60 minutes UV Curing, at 60°C) | 19.0 | J/m | ASTM D256A |
| Hardness (60 minutes UV Curing, at 60°C) | 93.0 | Shore D | ASTM D2240 |
| Water Sorption (60 minutes UV Curing, at 60°C) | 0.67 | % | ASTM D570-98 |
| Linear Shrinkage During Printing (60 minutes UV Curing, at 60°C) | max. 0.1 | % | Internal Method |
| Linear Shrinkage During UV-curing (60 minutes UV Curing, at 60°C) | 0.5 | % | Internal Method |
| Linear Shrinkage During Thermal Cure (60 minutes UV Curing, at 60°C) | 0.1 | % | Internal Method |
| Compression Strength (60 minutes UV Curing, at 60°C) | 155.0 | MPa | ASTM D695 |
| Solid Density (60 minutes UV Curing, at 60°C) | 1.62 | g/cm³ | Internal Method |
| Tensile Strength (2 hours Thermal Curing, at 100°C) | 70 - 85 | MPa | ASTM D638 |
| Tensile Modulus (2 hours Thermal Curing, at 100°C) | 8.5 - 9.5 | GPa | ASTM D638 |
| Elongation at Break (2 hours Thermal Curing, at 100°C) | 1.0 | % | ASTM D638 |
| Flexural Strength (2 hours Thermal Curing, at 100°C) | 150 - 170 | MPa | ASTM D790 |
| Flexural Modulus (2 hours Thermal Curing, at 100°C) | 8.5 - 9.5 | GPa | ASTM D790 |
| Notched Izod Impact (2 hours Thermal Curing, at 100°C) | 18.0 | J/m | ASTM D256A |
| Hardness (2 hours Thermal Curing, at 100°C) | 94.0 | Shore D | ASTM D2240 |
| Water Sorption (2 hours Thermal Curing, at 100°C) | 0.59 | % | ASTM D570-98 |
| Linear Shrinkage During Printing (2 hours Thermal Curing, at 100°C) | max. 0.1 | % | Internal Method |
| Linear Shrinkage During UV-curing (2 hours Thermal Curing, at 100°C) | 0.5 | % | Internal Method |
| Linear Shrinkage During Thermal Cure (2 hours Thermal Curing, at 100°C) | 0.1 | % | Internal Method |
| Compression Strength (2 hours Thermal Curing, at 100°C) | 160.0 | MPa | ASTM D695 |
| Solid Density (2 hours Thermal Curing, at 100°C) | 1.62 | g/cm³ | Internal Method |
| Value | Units | Test Method / Conditions | |
| Density | 1.52 | g/cm³ | — |
| Viscosity | 1400.0 | cps | — |
| Critical Exposure Energy | 9.55 | mJ/cm² | — |
| Penetration Depth | 0.18 | mm | — |
Technical Details & Test Data
- 3D-Printer Compatibility
Printer name Printer Compatibility Atum3D DLP Station 5 Yes Shining3D AccuFab-L4K Yes Ackuretta Freeshape 120 Yes Prusa SL1 Yes Anycubic Photon Yes Anycubic Photon Mono Yes Anycubic Photon Mono SE Yes Anycubic Photon Mono X Yes Elegoo Mars Yes Elegoo Mars 2 Yes Elegoo Mars 3 Yes Elegoo Saturn Yes Phrozen Sonic Mini 4K Yes Phrozen Series Preliminary settings Peopoly Phenom Prime Yes Creality Halot-Sky Yes Creality LD-002H Yes Moonray S & D Not compatible Formlabs Form2 Not compatible Asiga Max UV & Pro 4K Not compatible 385 - 420nm MSLA, SLA & DLP printer
Safety & Health
- Hazard Statements
- H315: Causes skin irritation.
- H317: May cause an allergic skin reaction.
- H319: Causes serious eye irritation.