An extremely strong and easy to print Stereolithography (SLA) and Digital Light Processing (DLP) resin which is perfect for industrial applications.
- Key Benefits
- High strength
- High temperature resistance
- Low odor
- Low shrinkage
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Appearance
- Opaque grey liquid
- Mechanical Properties
- Typical Properties
- Note
*Parts were washed in Isopropyl alcohol and post-cured in a Wicked Engineering Curebox. Values may vary depending on individual machine processing and post-curing.
Value | Units | Test Method / Conditions | |
Tensile Strength (30 minutes High Power LED Curing, at 60°C) | 52 - 70 | MPa | ASTM D638 |
Tensile Modulus (30 minutes High Power LED Curing, at 60°C) | 2.9 - 3.2 | GPa | ASTM D638 |
Elongation at Break (30 minutes High Power LED Curing, at 60°C) | 4 - 8 | % | ASTM D638 |
Flexural Strength (30 minutes High Power LED Curing, at 60°C) | 121 - 130 | MPa | ASTM D790 |
Flexural Modulus (30 minutes High Power LED Curing, at 60°C) | 3.1 - 3.3 | GPa | ASTM D790 |
Notched Izod Impact (30 minutes High Power LED Curing, at 60°C) | 20.0 | J/m | ASTM D256A |
Hardness (30 minutes High Power LED Curing, at 60°C) | 87.0 | Shore D | ASTM D2240 |
Water Sorption (30 minutes High Power LED Curing, at 60°C) | 0.45 | % | ASTM D570-98 |
Tensile Strength (120 minutes High Power LED Curing, at 60°C) | 60 - 84 | MPa | ASTM D638 |
Tensile Modulus (120 minutes High Power LED Curing, at 60°C) | 3.1 - 3.4 | GPa | ASTM D638 |
Elongation at Break (120 minutes High Power LED Curing, at 60°C) | 3 - 6 | % | ASTM D638 |
Flexural Strength (120 minutes High Power LED Curing, at 60°C) | 134 - 140 | MPa | ASTM D790 |
Flexural Modulus (120 minutes High Power LED Curing, at 60°C) | 3.3 - 3.5 | GPa | ASTM D790 |
Notched Izod Impact (120 minutes High Power LED Curing, at 60°C) | 17.0 | J/m | ASTM D256A |
Hardness (120 minutes High Power LED Curing, at 60°C) | 90.0 | Shore D | ASTM D2240 |
Water Sorption (120 minutes High Power LED Curing, at 60°C) | 0.39 | % | ASTM D570-98 |
Glass Transition Temperature (120 minutes High Power LED Curing, at 60°C) | 128.0 | °C | ASTM D7028 |
Value | Units | Test Method / Conditions | |
Density | 1.12 | g/cm³ | — |
Viscosity | 550.0 | cps | — |
Critical Exposure Energy | 9.88 | mJ/cm² | — |
Penetration Depth | 0.2 | mm | — |
Technical Details & Test Data
- 3D-Printer Compatibility
Printer name Printer Compatibility Moonray S & D Yes Formlabs Form 2 Yes Formlabs Form 1+ Yes DWS Digital Wax 028 Yes Carima IM2 Yes W2P SolFlex Series Yes W2P Sollab Series Yes Ackuretta Freeshape 120 Yes Miicraft 125 Yes Miicraft Ultra Yes Miicraft Prime Yes Asiga Max UV Yes Asiga Pro 4K Yes Peopoly Moai Yes Peopoly Phenom Prime Yes Atum3D DLP Station 5 Yes Shining3D AccuFab-L4K Yes Anycubic Photon Yes Anycubic Photon Mono Yes Anycubic Photon Mono SE Yes Anycubic Photon Mono X Yes Anycubic Photon M3 Available Soon Anycubic Photon M3 Plus Yes Creality Halot-Sky Yes Creality Halot-One Yes Elegoo Mars Yes Elegoo Mars 2 Yes Elegoo Mars 3 Yes Elegoo Saturn Yes Phrozen Sonic Mini 4K Yes Phrozen Shuffle Yes Phrozen Sonic Mighty 4K Yes Phrozen Series Preliminary settings Prusa SL1Speed Yes Zortrax Inkspire Yes Uniz Slash Yes Kudo3D Bean Yes Wanhao D7 Yes XYZ Nobel 1.0A Yes Beam3D Prism Yes Epax3D X1N Yes Epax3D X10 Color Yes Epax X10 & E10 Mono Yes Epax X1K E6 Yes 385 - 420nm MSLA, SLA & DLP printer - Liqcreate Strong-X for Injection Molding
Liqcreate Strong-X is the ideal material for low-volume injection molding. A wide range of thermoplastic polymers have been tested on compatibility with molds made from Liqcreate Strong-X. The focus of this study was on temperature resistance of the 3D-printed molds and on adhesion of the thermoplastic polymer to the mold.
The tested polymers are listed in the table below and include PP, PE, HDPE, ABS, PETG, PA6 and PA12 co-polymer, injected at temperatures between 230 and 280°C (446 - 536°F). All materials were injected without any mold release agents.
Thermal degradation of the 3D-printed mold has not been observed in any of the tests. Polymers like ABS, PA6 and PA12 show adhesion to the mold, while other polymers like PP, PE, HDPE and PETG release easily from the mold and are compatible with Strong-X 3Dprinted molds. The test results were obtained with the use of two three-dimensional molds from Strong-X, and therefore a mirror plate is not used. Over 100 injections were successfully done with HDPE, PE and PP.
Polymer Injection Temperature Polymer Adhesion to Mold PP* 230°C/446°F No adhesion PE 240°C/464°F No adhesion HDPE 240°C/464°F No adhesion ABS 260°C/500°F Medium adhesion PETG 260°C/500°F No adhesion PA6 280°C/536°F Medium adhesion PA12* 280°C/536°F Medium adhesion Table 1. Injection molding results**
* Tested by industrial partner CompriseTec GmbH.
** The results may vary and depending on post-curing, choice of polymer, mold design, and machine processing.
Safety & Health
- Hazard Statements
- H315: Causes skin irritation.
- H317: May cause an allergic skin reaction.
- H319: Causes serious eye irritation.
- H411: Toxic to aquatic life with long lasting effects.
Packaging & Availability
- Packaging Information
- Liqcreate Strong-X 250 gram (Order number LSX00250)
- Liqcreate Strong-X 1 kg (Order number LSX01000)