Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (50 mm/min) | 55 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 38 | MPa | ISO 527 |
| Rockwell Hardness | 115 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2600 | MPa | ASTM D638 |
| Tensile Strain at Break (50 mm/min) | 10 | % | ISO 527-2/1A |
| Flexural Strength (2 mm/min) | 86 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2700 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 16 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 13 | kJ/m2 | ISO 180 1A |
| Value | Units | Test Method / Conditions | |
| Specific Gravity (Natural or representative color) | 1.05 | - | ISO 1183 |
| Melt Flow Index - MFI (200°C/5 kg) | 2.6 | g/10 min | ASTM D 1238 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.2 - 0.5 | % | ISO 294-4 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.2 - 0.5 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 92 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 80 | °C | ISO 75-2 |
| Vicat Softening Temperature (B/50) | 99 | °C | ISO 306 |