Value | Units | Test Method / Conditions | |
Tensile Strength at Yield (50 mm/min) | 50 | MPa | ISO 527 |
Tensile Strength at Break (50 mm/min) | 40 | MPa | ISO 527 |
Rockwell Hardness | 111 | Scale R | ASTM D785 |
Tensile Modulus (50 mm/min) | 2500 | MPa | ASTM D638 |
Tensile Strain at Break (50 mm/min) | 9.5 | % | ISO 527 |
Flexural Strength (2 mm/min) | 79 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 2600 | MPa | ISO 178 |
Charpy Impact Strength - V-notched (23°C, 4mm) | 15 | kJ/m2 | ISO 179 1eA |
Notched Izod Impact Strength (23°C, 4 mm) | 14 | kJ/m2 | ISO 180 1A |
Value | Units | Test Method / Conditions | |
Specific Gravity (Natural or representative color) | 1.05 | - | ISO 1183 |
Melt Flow Index - MFI (220°C/10 kg) | 29 | g/10 min | ISO 1133 |
Melt Flow Index - MFI | 0.34~0.42 | g/10 min | ISO 1133 |
Molding Shrinkage - MD | 0.35~0.43 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 90 | °C | ISO 75-2 |
Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 77 | °C | ISO 75-2 |
Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm) | 95 | °C | ISO 75-2 |
Heat Deflection Temperature - HDT (0.45 MPa, Annealed, 4 mm) | 99 | °C | ISO 75-2 |