Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Extrusion Molding
Applications & Uses
- Plastics & Elastomers Processing Methods
- Applications
• Sheet
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Sheet Extrusion)
- Impact Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus | 2030 | MPa | ASTM D638 |
Tensile Strength (Yield) | 39 | MPa | ASTM D638 |
Tensile Strength (Break) | 28 | MPa | ASTM D638 |
Tensile Elongation (Yield) | 3.1 | % | ASTM D638 |
Tensile Elongation (Break) | 32 | % | ASTM D638 |
Tensile Elongation (Break) | 31.6 | % | ASTM D638 |
Flexural Modulus | 2100 | MPa | ASTM D790 |
Flexural Strength | 63 | MPa | ASTM D790 |
Notched Izod Impact | 410 | J/m | ASTM D256 |
Instrumented Dart Impact | 33 | J | ASTM D3763 |
Tensile Stress (Break) | 28 | MPa | ASTM D638 |
Tensile Stress (Yield) | 39 | MPa | ASTM D638 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate | 4 | g/10 min | ASTM D1238 |
Density/Specific Gravity | 1.03 | g/cm3 | ASTM D792 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature | 106 | °C | ASTM D1525 |
CLTE - Flow (-40 to 40°C) | 0.0001 | cm/cm/°C | — |
CLTE - Transverse (-40 to 40°C) | 0.0001 | cm/cm/°C | — |
Relative Thermal Index Electric | 60 | °C | UL 746B |
Relative Thermal Index Impact | 60 | °C | UL 746B |
Relative Thermal Index Strength | 60 | °C | UL 746B |
Deflection Temperature (0.45 MPa, Unannealed, 3.20 mm) | 93 | °C | ASTM D648 |
Deflection Temperature (1.8 MPa, Unannealed, 3.20 mm) | 80 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Adapter Temperature | 205 to 250 | °C | — |
Barrel- Zone 1 Temp | 170 to 200 | °C | — |
Barrel- Zone 2 Temp | 180 to 220 | °C | — |
Barrel- Zone 3 Temp | 190 to 225 | °C | — |
Barrel- Zone 4 Temp | 200 to 250 | °C | — |
Die Temp | 205 to 250 | °C | — |
Drying Temperature | 80 to 95 | °C | — |
Drying Time | 4 | hours | — |
Roll Stack Temperature Bottom | 100 to 105 | °C | — |
Roll Stack Temperature Middle | 95 to 105 | °C | — |
Roll Stack Temperature Top | 90 to 95 | °C | — |
Suggested Max Moisture | 0.02 | % | — |
Value | Units | Test Method / Conditions | |
CLTE (Flow: -40 to 40°C) | 0.000101 | cm/cm/°C | ASTM D1525 |
CLTE (Transverse: -40 to 40°C) | 0.000104 | cm/cm/°C | ASTM D1525 |
Dart Impact | 33 | J | ASTM D3763 |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.2 mm) | 93 | °C | ASTM D648 |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.2 mm) | 80 | °C | ASTM D648 |
Flame Rating (1.5mm) | HB | — | UL 94 |
Notched Izod Impact | 411 | J/m | ASTM D256 |
RTi | 60 | °C | UL 746 |
Vicat Softening Temperature | 106 | °C | ASTM D256 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
- Availability
Global