Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Flammability
- Impact Properties
Value | Units | Test Method / Conditions | |
Density | 1.4 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate | 8 | g/10 min | ASTM D1238 |
Specific Gravity | 1.4 | g/cm³ | ASTM D792 |
Density/Specific Gravity | 1240 | kg/m3 | ISO 1183 |
Molding Shrinkage (Lateral (24 hr)) | 0.6 to 0.8 | % | ISO 294-4 |
Molding Shrinkage (Lengthwise (24 hr)) | 0.2 to 0.4 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Tensile Strength (Yield at 3.18 mm) | 93.1 | MPa | ASTM D638 |
Tensile Strength (Break at 3.18 mm) | 93.1 | MPa | ASTM D638 |
Flexural Modulus (3.18 mm) | 4830 | MPa | ASTM D790 |
Flexural Strength (3.18 mm) | 145 | MPa | ASTM D790 |
Notched Izod Impact | 53 | J/m | ASTM D256 |
Flexural Strength | 170 | MPa | ISO 178 |
Tensile Elongation (Break) | 3.5 | % | ISO 527 |
Tensile Modulus | 5700 | MPa | ISO 527 |
Tensile Modulus (23°C) | 5500 | MPa | ISO 178 |
Tensile strength (Break) | 115 | MPa | ISO 527 |
Value | Units | Test Method / Conditions | |
Deflection Temperature (0.45 MPa, Unannealed, 3.20 mm) | 204 | °C | ASTM D648 |
Deflection Temperature (1.8 MPa, Unannealed, 3.20 mm) | 188 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.5mm) | HB | - | UL 94 |
Value | Units | Test Method / Conditions | |
Charpay impact strength | 45 | kJ/m2 | ISO 179/1eU |
Charpy notched impact | 6 | kJ/m2 | ISO 179/1eA |
DSC (Melt Point) | 221 | °C | ISO 11357 |
HDT/A (1,8 MPa) | 200 | °C | ISO 75-1/-2 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
- Availability
Global