Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- General Purpose
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Impact Properties
Value | Units | Test Method / Conditions | |
Density | 1.41 | g/cm³ | ISO 1183 |
Melt Volume-Flow Rate | 8 | cm³/10min | ISO 1133 |
Melt Volume-Flow Rate | 8 | cm3/10min | ISO 1183 |
Water Absorption (Saturation at 23°C) | 0.75 | % | ISO 62 |
Water Absorption (Equilibrium at 23°C 50% RH) | 0.2 | % | ISO 62 |
Molding Shrinkage (Across Flow : at 23°C) | 1.9 | % | — |
Molding Shrinkage (Flow : at 23°C) | 2 | % | — |
Density/Specific Gravity | 1.41 | g/cm3 | ISO 1183 |
Tensile Modulus (at 23°C) | 2760 | MPa | ISO 527-1/1A |
Molding Shrinkage (Across Flow: 23°C) | 1.9 | % | ISO 294-4 |
Molding Shrinkage (Flow: 23°C) | 2 | % | ISO 294-4 |
Water Absorption (Equilibrium, 23°C) | 0.2 | % | ISO 62 |
Water Absorption (Saturation, 23°C) | 0.75 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield at 23°C) | 65 | MPa | ISO 527-2/1A/50 |
Tensile Strain (Break at 23°C) | 10 | % | ISO 527-2/1A/50 |
Charpy Notched Impact Strength (at 23°C) | 6 | kJ/m | ISO 179/1eA |
Tensile Modulus (23°C) | 2760 | MPa | ISO 527-2/ |
Charpy Unnotched Impact Strength (at 23°C) | 190 | kJ/m | ISO 179/1eU |
Tensile Strain (Break, 23°C) | 10 | % | ISO 527-2/1A/50 |
Tensile Stress (Yield, 23°C) | 65 | MPa | ISO 527-2/1A/50 |
Value | Units | Test Method / Conditions | |
Deflection Temperature (0.45 MPa, Unannealed, 3.20 mm) | 158 | °C | ISO 75-2/B |
Deflection Temperature (1.8 MPa, Unannealed, 3.20 mm) | 101 | °C | ISO 75-2/A |
Vicat Softening Temperature | 161 | °C | ISO 306/B50 |
Melting Temperature | 166 | °C | ISO 11357-3 |
CLTE - Flow | 0.00012 | cm/cm/°C | ISO 11359-2 |
CLTE - Transverse | 0.00012 | cm/cm/°C | ISO 11359-2 |
CLTE (Flow) | 0.00012 | cm/cm/°C | ISO 11359-2 |
CLTE (Transverse) | 0.00012 | cm/cm/°C | ISO 11359-2 |
Heat Deflection Temperature (0.45 MPa, Unannealed) | 158 | °C | ISO 75-2/B |
Heat Deflection Temperature (1.8 MPa, Unannealed) | 101 | °C | ISO 75-2/A |
Value | Units | Test Method / Conditions | |
Notched Izod Impact (23°C) | 6 | kJ/m2 | ISO 179/1eA |
Unnotched Impact Strength (23°C) | 190 | kJ/m2 | ISO 179/1eU |
Packaging & Availability
- Country Availability
- Regional Availability
- Availability
Global