Value | Units | Test Method / Conditions | |
Glass Transition Temperature (DMA, Dry) (DMA, Wet (60°C, 90% RH)) (DMA after TOS (260°C, 1000 hrs)) | 305 (250) (310) | °C | — |
Thermal Oxidative Stability (260°C, 1000 hrs) | 1.1 | % wt loss | — |
Moisture Uptake (60oC, 90% RH) | 1.2 | % wt gain | — |
Fiber Volume (ASTM D3171‐99) | 56 | % | — |
Value | Units | Test Method / Conditions | |
Solution Solids Content (204°C/180 min cure) | 60 ‐ 65 | % | — |
Solution Density (Room Temperature) | 1.05 ‐ 1.10 | g/mL | — |
Solution Viscosity (Room Temp, Brookfield spindle #RV‐4, 100 rpm) | 250 ‐ 650 | cP | — |
Powder Melt Viscosity (274°C, Brookfield spindle #27, 50 rpm) | 300 ‐ 600 | cP | — |
Powder Volatile Content (TGA ramp to 316°C) | 4 ‐ 6 | % | — |
Technical Details & Test Data
- Mechanical Properties – Composite
Composite Properties Test Parameters Typical Values (MPa) Typical Values (ksi) Compression Strength RT, Dry 656 95 Compression Strength 260oC, Dry 444 64 Compression Strength RT, Wet (60°C, 90% RH) 663 96 Compression Strength 260oC, Wet (60°C, 90% RH) 282 41 Compression Strength 260oC , after TOS (260°C, 1000 hrs) 440 64 Interlaminar Shear Strength RT, Dry 50.3 7.3 Interlaminar Shear Strength 260°C, Dry 37.2 5.4 Interlaminar Shear Strength RT, Wet (60°C, 90% RH) 53.7 7.8 Interlaminar Shear Strength 260oC, Wet (60°C, 90% RH) 22.7 3.3 Interlaminar Shear Strength RT, after TOS (260°C, 1000 hrs) 46.2 6.7 Interlaminar Shear Strength 260oC, after TOS (260°C, 1000 hrs) 37.9 5.5