| Value | Units | Test Method / Conditions | |
| MFR load | 5 | kg | -- |
| MFR temperature | 240 | °C | -- |
| Melt Mass Flow Rate - MFR (240°C/5 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage - lengthwise (24h) | 0.5 | % | ISO 294-4, 2577 |
| Density | 1170 | kg/m3 | ASTM D 792 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 45 | MPa | ASTM D638 |
| Tensile Modulus | 2300 | MPa | ISO 527 |
| Charpy Notched Impact Strength | 25 | kJ/m2 | ISO 179 |
| Charpy Impact Strength | 100 | kJ/m2 | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 25 | kJ/m2 | ISO 180 |
| Charpy Notched Impact Strength (-30°C) | 70 | kJ/m2 | ISO 179/1eU |
| Unnotched Izod Imact Strength | 100 | kJ/m2 | ISO 180/1U |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (A50) | 115 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Burning Behavior (1.5 mm) | HB | - | UL 94 |
| Burning Behavior at Thickness - tested | 1.5 | mm | -- |
| Value | Units | Test Method / Conditions | |
| Pre-drying Temperature | 100 - 110 | °C | -- |
| Pre-drying Time | 4 | h | -- |
| Processing Humidity | ≤0.02 | % | -- |
| Mold temperature | 70 - 90 | °C | -- |
| Melt Temperature | 240 - 260 | °C | -- |