R25MLT-MG is highly transparent random copolymer resin containing anti-static agent. Produced using Spheripol® technology, the grade has an exceptional advantage of having morphologically uniform resins, and intrinsically organoleptic-neutral (odorless) character. The ultra clear nucleation additive package also ensure excellent dimensional stability and potential for energy and cycle tine savings. Without exception, all potential activities for applications of this grade in the healthcare area have to be discussed with the relevant technical and business representative of NATPET. NATPET prohibits the use of this product in an implantable device that is introduced into the human body by surgical intervention and is intended to remain in place following surgical procedure.
- Special Features
- Amazing result on transparent articles
- Shows broad processing window while providing excellent clarity at low molding temperature
- Tested for biocompatibility, ISO 10993 (Biological Evaluation of Medical Devices). Refer RCPD.
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers Processing Methods
- Processing Methods
Injection Molding
- Processing Conditions
Average extruder temperature range may be kept between 190 - 210°C.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Density 23°C | 0.9 | g/cm³ | ISO. 1183 |
| Melt Flow Rate (MFR) 230°C/2.16 kg | 25 | g/10-min | ASTM D 1238-13 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Tensile Modulus 1-mm/min | 1150 | MPa | ISO 527 |
| Tensile Stress at Yield 50-mm/min | 29 | MPa | ISO 527 |
| Tensile Strain at Break 50-mm/min | min. 50 | % | ISO 527 |
| Tensile Strain at Yield 50-mm/min | 17 | % | ISO 527 |
| Charpy un-notched " 23 °C, Type 1, Edgewise | 200 | KJ/㎡ | ISO. 179 |
| Charpy un-notched 0 °C, Type 1, Edgewise | 70 | KJ/㎡ | ISO. 179 |
| Charpy notched 23 °C, Type 1, Edgewise | 6 | KJ/㎡ | ISO 179 |
| Charpy notched 0 °C, Type 1, Edgewise | 3 | KJ/㎡ | ISO. 179 |
| IZOd Notched 23°C | 5.4 | KJ/㎡ | ISO 180 |
| Heat Deflection Temperature 0.45 MPa Un-annealed | 76 | °C | ISO 75B |
| Vicat Softening Temperature A50 (50°C/h 10N) | 130 | °c | ISO 306 |
| Haze 1.0mm | 6 | % | ASTM D 1003 |
Regulatory & Compliance
- Food Regulations
This product is defined as a preparation under specific food contact regulation. Detailed information will be provided in a relevant document “Regulatory Compliances Product Declaration (RCPD)’ upon request.
Storage & Handling
- Storage and Handling
lf the resin is stored under adverse conditions, i.e. if there are large fluctuations in ambient temperature and the atmospheric humidity is high, moisture may condense inside the packaging. Under these circumstances, it is recormmended to dry the resin before use. Unfavorable storage conditions may also intensify the resin’s slight characteristic odor. Polypropylene resin should be stored to prevent a direct exposure to sunlight (UV) and heat. Improper storage can initiate degradation. Therefore the resin must be protected from direct sunlight, temperatures above 40°C and high atmospheric humidity during storage. The resin can be stored over a period of more than 6 month without significant changes in the specified properties, appropriate storage conditions provided. Higher storage temperatures reduce the storage time. Please refer to Safety Data Sheet (SDS) for handling and storage information.