Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
Properties
- Mechanical Properties
- Typical Properties
- Thermal Properties
Value | Units | Test Method / Conditions | |
Tensile Stress at yield at 23°C (50 mm/min) | 60 | MPa | ISO 527-1/2 |
Tensile Stress at yield (23°C, 50mm/min) | 60 | MPa | ISO 527-1/2 |
Tensile Stress at Break at 23°C | 45 | MPa | ISO 527-1/2 |
Tensile Stress at Break (23°C) | 45 | MPa | ISO 527-1/2 |
Tensile Strain at Break (23°C) | min. 10 | % | ISO 527-1/2 |
Tensile Elastic modulus 23°C (1 mm/min) | 3000 | MPa | ISO 527-1/2 |
Tensile Elastic Modulus (23°C, 1mm/min) | 3000 | MPa | ISO 527-1/2 |
Izod Impact Strength Notched at 23°C | 5 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (23°C) | 5 | kJ/m2 | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Density at 23°C | 1.13 | g/cm3 | ISO 1183 |
Density (23°C) | 1.13 | g/cm3 | ISO 1183 |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 1.0 – 1.5 | % | Internal |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 1.0 - 1.5 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 1.0 – 1.5 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 1.0 - 1.5 | % | Internal |
Drying Temperature | 80 | °C | — |
Drying Time | 4 | h | — |
Melt Temperature | 240 - 270 | °C | — |
Mould Temperature | 60 - 90 | °C | — |
Value | Units | Test Method / Conditions | |
VICAT Softening Point (50 N, 50°C/h) | 190 | °C | ISO 306/B |
VICAT Softening Point (50N, 50°C/h) | 190 | °C | ISO 306/B |
Heat Deflection Temperature (1,80 MPa - 120°C/h) | 60 | °C | ISO 75-1/-2 |
Heat Deflection Temperature (1.80 MPa, 120°C/h) | 60 | °C | ISO 75-1/-2 |
Regulatory & Compliance
- Certifications & Compliance