Nevies 042 FV17 NERO

Identification & Functionality

Chemical Family

Acrylonitrile Butadiene Styrene (ABS),

Styrenics

Fillers Included

Glass Fiber

Polymer Name

Acrylonitrile Butadiene Styrene (ABS)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Materials Features

Good Aesthetics,

Low Warpage

Applications & Uses

Markets

Consumer Goods

Applications

Consumer Goods — Other Consumer Goods Applications

Plastics & Elastomers End Uses

Consumer Applications

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress at Break at 23°C	70	MPa	ISO 527-1/2
Tensile Stress at Break (23°C, 5mm/min)	70	MPa	ISO 527-1/2
Tensile Strain at Break at 23°C (1 mm/min)	3.5	%	ISO 527-1/2
Tensile Strain at Break (23°C, 1mm/min)	3.5	%	ISO 527-1/2
Tensile Elastic modulus 23°C (1 mm/min)	6400	MPa	ISO 527-1/2
Tensile Elastic Modulus (23°C, 1mm/min)	6400	MPa	ISO 527-1/2
FLEXURAL Elastic Modulus	5500	MPa	ISO 178
Flexural Elastic Modulus	5500	MPa	ISO 178
Izod Impact Strength Unnotched at 23°C	15	kJ/m2	ISO 180/1U
Izod Impact Strength Unnotched (23°C)	15	kJ/m2	ISO 180/1U
Izod Impact Strength Notched at 23°C	5.5	kJ/m2	ISO 180/1A
Izod Impact Strength Notched (23°C)	5.5	kJ/m2	ISO 180/1A

Typical Properties

	Value	Units	Test Method / Conditions
Density at 23°C	1.16	g/cm3	ISO 1183
Density (23°C)	1.16	g/cm3	ISO 1183
Melt Volume Flow Rate - MVR at 220°C, 10 kg)	8	cm3/10min	ISO 1183
Melt Volume Flow Rate (220°C, 10 kg)	8	cm3/10min	ISO 1183
Drying Temperature	80	°C	—
Drying Time	4	h	—
Melt Temperature	220 - 260	°C	—
Mould Temperature	50 - 90	°C	—

Thermal Properties

	Value	Units	Test Method / Conditions
VICAT Softening Point (50 N, 50°C/h)	95	°C	ISO 306/B
VICAT Softening Point (50N, 50°C/h)	95	°C	ISO 306/B

Other Properties

	Value	Units	Test Method / Conditions
Burning Behaviour (1.6 mm)	HB	—	—

Regulatory & Compliance

Certifications & Compliance

UL 94