Nevies 4252 CR NATURALE

Identification & Functionality

Chemical Family

Acrylonitrile Butadiene Styrene (ABS),

Styrenics

Polymer Name

Acrylonitrile Butadiene Styrene (ABS)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Materials Features

Good Aesthetics,

Low Warpage

Applications & Uses

Markets

Consumer Goods

Applications

Consumer Goods — Other Consumer Goods Applications

Plastics & Elastomers End Uses

Consumer Applications

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress at yield at 23°C (5 mm/min)	50	MPa	ISO 527-1/2
Tensile Stress at yield (23°C, 5mm/min)	50	MPa	ISO 527-1/2
Tensile Stress at Break at 23°C	35	MPa	ISO 527-1/2
Tensile Stress at Break (23°C, 5mm/min)	35	MPa	ISO 527-1/2
Tensile Strain at Break at 23°C	15	%	ISO 527-1/2
Tensile Strain at Break (23°C, 5mm/min)	15	%	ISO 527-1/2
FLEXURAL Elastic Modulus	2100	MPa	ISO 178
FLEXURAL Elastic Modulus (2mm/min)	2100	MPa	ISO 178
Izod Impact Strength Notched at 23°C	20	kJ/m2	ISO 180/1A
Izod Impact Strength Notched (23°C, 80 x 10 x 4.0 mm)	20	kJ/m2	ISO 180/1A
Rockwell (scale)	110	-	ISO 2039-2

Typical Properties

	Value	Units	Test Method / Conditions
Density at 23°C	1,04	g/cm3	ISO 1183
Density (23°C)	1.04	g/cm3	ISO 1183
Melt Volume Flow Rate - MVR at 220°C, 10 kg)	20	cm3/10min	ISO 1183
Melt Volume Flow Rate (220°C, 10 kg)	20	cm3/10min	ISO 1183
Drying Temperature	80	°C	-
Melt Temperature	200 - 240	°C	-
Mould Temperature	30 - 70	°C	-

Thermal Properties

	Value	Units	Test Method / Conditions
VICAT Softening Point (50 N - 50°C/h)	105	°C	ISO 306/B
VICAT Softening Point (50N, 50°C/h)	105	°C	ISO 306/B
Temp. of Deflection Under Load (1,80 MPa - 120°C/h)	85	°C	ISO 75/Be

Other Properties

	Value	Units	Test Method / Conditions
Flammability (Thickness 1,6 mm)	HB	class	UL94
Flammability (Thickness 1.6 mm)	HB	class	UL94

Regulatory & Compliance

Certifications & Compliance

UL 94