Value | Units | Test Method / Conditions | |
Tensile Stress at Break at 23°C | 55 | MPa | ISO 527-1/2 |
Tensile Stress at Break (23°C, 5mm/min) | 55 | MPa | ISO 527-1/2 |
Tensile Elastic modulus 23°C (1 mm/min) | 4200 | MPa | ISO 527-1/2 |
Tensile Elastic Modulus (23°C, 1mm/min) | 4200 | MPa | ISO 527-1/2 |
FLEXURAL Elastic Modulus at 23°C | 3400 | MPa | ISO 178 |
FLEXURAL Elastic Modulus at 23°C (2mm/min) | 3400 | MPa | ISO 178 |
Izod Impact Strength Unnotched at 23°C | 35 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Unnotched (23°C) | 35 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Notched at 23°C | 4 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (23°C) | 4 | kJ/m2 | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Density at 23°C | 1.16 | g/cm3 | ISO 1183 |
Density (23°C) | 1.16 | g/cm3 | ISO 1183 |
Drying Temperature | 80 | °C | — |
Drying Time | 4 | h | — |
Melt Temperature | 250 - 280 | °C | — |
Mould Temperature | 70 - 100 | °C | — |