Value | Units | Test Method / Conditions | |
Tensile Stress at Break at 23°C | 130 | MPa | ISO 527-1/2 |
Tensile Stress at Break (23°C, 5mm/min) | 130 | MPa | ISO 527-1/2 |
Tensile Strain at Break at 23°C | 5 | % | ISO 527-1/2 |
Tensile Strain at Break (23°C, 5mm/min) | 5 | % | ISO 527-1/2 |
Tensile Elastic modulus 23°C (1 mm/min) | 7000 | MPa | ISO 527-1/2 |
Tensile Elastic Modulus (23°C, 1mm/min) | 7000 | MPa | ISO 527-1/2 |
Flexural Maximum Strength at 23°C (2 Mm/Min) | 180 | MPa | ISO 178 |
Flexural Maximum Strength at 23°C (2 mm/Min) | 180 | MPa | ISO 178 |
FLEXURAL Elastic Modulus at 23°C | 6000 | MPa | ISO 178 |
FLEXURAL Elastic Modulus at 23°C (2mm/min) | 6000 | MPa | ISO 178 |
Izod Impact Strength unnotched at 23°C (80 x 10 x 4.0 mm) | 75 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Unnotched (23°C, 80 x 10 x 4.0 mm) | 75 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Notched at 23°C (80 x 10 x 4.0 mm) | 6 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (23°C, 80 x 10 x 4.0 mm) | 6 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched at -23°C (127x12.7x3.2 mm) | 50 | J/m | ASTM D256 |
Izod Impact Strength Notched ((-23°C), 127x12.7x3.2 mm) | 50 | J/m | ASTM D256 |
Hardness Rockwell (15 sec) | 115 | Scale R | ISO 2039-2 |
Value | Units | Test Method / Conditions | |
Density at 23°C | 1,23 | g/cm3 | ISO 1183 |
Density (23°C) | 1.23 | g/cm3 | ISO 1183 |
Moisture Absorption (23°C, 50% UR-HR) | 0,2 - 0,4 | % | ISO 62 |
Moisture Absorption (23°C, 50% UR-HR) | 0.2 - 0.4 | % | ISO 62 |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 0,9 - 1,3 | % | Internal |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.9 - 1.3 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 2,5 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 2.5 | % | Internal |
Drying Temperature | 80 | °C | — |
Melt Temperature | 240 - 280 | °C | — |
Mould Temperature | 70 - 100 | °C | — |
Value | Units | Test Method / Conditions | |
VICAT Softening Point (10 N - 50°C/h) | 215 | °C | ISO 306/A |
VICAT Softening Point (10N, 50°C/h) | 215 | °C | ISO 306/A |
VICAT Softening Point (50 N - 50°C/h) | 205 | °C | ISO 306/B |
VICAT Softening Point (50N, 50°C/h) | 205 | °C | ISO 306/B |
Heat Deflection Temperature (0,45 MPa - 120°C/h) | 210 | °C | ISO 75/Be |
Heat Deflection Temperature (0.45 MPa, 120°C/h) | 210 | °C | ISO 75/Be |
Heat Deflection Temperature (1,80 MPa - 120°C/h) | 190 | °C | ISO 75/Ae |
Heat Deflection Temperature (1.80 MPa, 120°C/h) | 190 | °C | ISO 75/Ae |
Value | Units | Test Method / Conditions | |
Flammability (Thickness 1,6 mm) | HB | class | UL94 |
Flammability (Thickness 3.2 mm) | HB | class | UL94 |