Value | Units | Test Method / Conditions | |
Tensile Stress at yield at 23°C (5 mm/min) | 55 | MPa | ISO 527-1/2 |
Tensile Stress at yield (23°C, 5mm/min) | 55 | MPa | ISO 527-1/2 |
Tensile Strain at yield at 23°C | 5 | % | ISO 527-1/2 |
Tensile Strain at Yield (23°C, 50mm/min) | 5 | % | ISO 527-1/2 |
Tensile Stress at Break at 23°C | 40 | MPa | ISO 527-1/2 |
Tensile Stress at Break (23°C, 5mm/min) | 40 | MPa | ISO 527-1/2 |
Tensile Strain at Break (23°C, 5mm/min) | min. 15 | % | ISO 527-1/2 |
Tensile Elastic modulus 23°C (1 mm/min) | 2300 | MPa | ISO 527-1/2 |
Tensile Elastic Modulus (23°C, 1mm/min) | 2300 | MPa | ISO 527-1/2 |
Tensile Strain at Break (23°C) | min. 15 | % | ISO 527-1/2 |
FLEXURAL Elastic Modulus at 23°C | 2000 | MPa | ISO 178 |
Izod Impact Strength Unnotched at 23°C | 25 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Unnotched (23°C) | 25 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Notched at 23°C | 15 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched at 23°C | 115 | J/m | ASTM D256 |
Izod Impact Strength Notched (23°C) | 15 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (23°C) | 115 | J/m | ASTM D256 |
Izod Impact Strength Notched at -20°C | 50 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (-20°C) | 50 | kJ/m2 | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Density at 23°C | 1.09 | g/cm3 | ISO 1183 |
Density (23°C) | 1.09 | g/cm3 | ISO 1183 |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 1.4 – 1.8 | % | Internal |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 1.4 - 1.8 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 1.4 – 1.8 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 1.4 - 1.8 | % | Internal |
Drying Temperature | 80 | °C | — |
Drying Time | 4 | h | — |
Melt Temperature | 230 - 270 | °C | — |
Mould Temperature | 60 - 90 | °C | — |
Value | Units | Test Method / Conditions | |
VICAT Softening Point (50 N - 50°C/h) | 165 | °C | ISO 306/B |
VICAT Softening Point (50N, 50°C/h) | 165 | °C | ISO 306/B |
Heat Deflection Temperature (1,80 MPa - 120°C/h) | 50 | °C | ISO 75-1/-2 |
Heat Deflection Temperature (1.80 MPa, 120°C/h) | 50 | °C | ISO 75-1/-2 |
Value | Units | Test Method / Conditions | |
Burning Behaviour | HB | — | UL94 |