Value | Units | Test Method / Conditions | |
Tensile Stress at Break at 23°C | 45 | MPa | ISO 527-1/2 |
Tensile Stress at Break (23°C) | 45 | MPa | ISO 527-1/2 |
Tensile Strain at Break (23°C) | min. 50 | % | ISO 527-1/2 |
Tensile Elastic modulus 23°C (1 mm/min) | 1800 | MPa | ISO 527-1/2 |
Tensile Elastic Modulus (23°C, 1mm/min) | 1800 | MPa | ISO 527-1/2 |
FLEXURAL Elastic Modulus at 23°C | 1500 | MPa | ISO 178 |
Izod Impact Strength Unnotched at 23°C | N.B. | kJ/m2 | ISO 180/1U |
Izod Impact Strength Unnotched (23°C) | N.B. | kJ/m2 | ISO 180/1U |
Izod Impact Strength Notched at 23°C | 90 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (23°C) | 90 | kJ/m2 | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Density at 23°C | 1.06 | g/cm3 | ISO 1183 |
Density (23°C) | 1.06 | g/cm3 | ISO 1183 |
Drying Temperature | 80 | °C | — |
Drying Time | 4 | h | — |
Melt Temperature | 260 - 290 | °C | — |
Mould Temperature | 70 - 90 | °C | — |
Value | Units | Test Method / Conditions | |
VICAT Softening Point (50 N - 50°C/h) | 180 | °C | ISO 306/B |
VICAT Softening Point (50N, 50°C/h) | 180 | °C | ISO 306/B |
Heat Deflection Temperature (1,80 MPa - 120°C/h) | 55 | °C | ISO 75-1/-2 |
Heat Deflection Temperature (1.80 MPa, 120°C/h) | 55 | °C | ISO 75-1/-2 |
Value | Units | Test Method / Conditions | |
Burning Behaviour | HB | — | UL94 |