Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
Properties
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Other Properties
Value | Units | Test Method / Conditions | |
Tensile Stress at Break at 23°C | 140 | MPa | ISO 527-1/2 |
Tensile Stress at Break (23°C, 5mm/min) | 140 | MPa | ISO 527-1/2 |
Tensile Strain at Break at 23°C | 4.5 | % | ISO 527-1/2 |
Tensile Strain at Break (23°C, 5mm/min) | 4.5 | % | ISO 527-1/2 |
Tensile Elastic modulus 23°C (1 mm/min) | 8500 | MPa | ISO 527-1/2 |
Tensile Elastic Modulus (23°C, 1mm/min) | 8500 | MPa | ISO 527-1/2 |
Izod Impact Strength unnotched at 23°C (80 x 10 x 4.0 mm) | 75 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Unnotched (23°C, 80 x 10 x 4.0 mm) | 75 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Notched at 23°C (80 x 10 x 4.0 mm) | 20 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (23°C, 80 x 10 x 4.0 mm) | 20 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched at 23°C (127x12.7x3.2 mm) | 70 | J/m | ASTM D256 |
Izod Impact Strength Notched (23°C, 127x12.7x3.2 mm) | 70 | J/m | ASTM D256 |
Hardness Rockwell | 115 | Scale R | ISO 2039-2 |
Value | Units | Test Method / Conditions | |
Density at 23°C | 1.33 | g/cm3 | ISO 1183 |
Density (23°C) | 1.33 | g/cm3 | ISO 1183 |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.3 – 0.6 | % | Internal |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.3 - 0.6 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 0.8 – 1.2 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 0.8 - 1.2 | % | Internal |
Drying Temperature | 80 | °C | — |
Drying Time | 4 | h | — |
Melt Temperature | 260 - 290 | °C | — |
Mould Temperature | 80 - 100 | °C | — |
Value | Units | Test Method / Conditions | |
VICAT Softening Point (50 N - 50°C/h) | 245 | °C | ISO 306/B |
VICAT Softening Point (50N, 50°C/h) | 245 | °C | ISO 306/B |
Heat Deflection Temperature (1,80 MPa - 120°C/h) | 240 | °C | ISO 75-1/-2 |
Heat Deflection Temperature (1.80 MPa, 120°C/h) | 240 | °C | ISO 75-1/-2 |
Value | Units | Test Method / Conditions | |
Flammability (Thickness 1,6 mm) | HB | class | UL94 |
Flammability (Thickness 1.6 mm) | HB | class | UL94 |
Regulatory & Compliance
- Certifications & Compliance