Value | Units | Test Method / Conditions | |
Tensile Stress at yield at 23°C (5 mm/min) | 70 | MPa | ISO 527-1/2 |
Tensile Stress at yield (23°C, 5mm/min) | 70 | MPa | ISO 527-1/2 |
Tensile Strain at yield at 23°C | 4 | % | ISO 527-1/2 |
Tensile Strain at Yield (23°C, 50mm/min) | 4 | % | ISO 527-1/2 |
Tensile Stress at Break at 23°C | 50 | MPa | ISO 527-1/2 |
Tensile Stress at Break (23°C, 5mm/min) | 50 | MPa | ISO 527-1/2 |
Tensile Strain at Break at 23°C | 30 | % | ISO 527-1/2 |
Tensile Strain at Break (23°C, 5mm/min) | 30 | % | ISO 527-1/2 |
Tensile Elastic modulus 23°C (1 mm/min) | 2700 | MPa | ISO 527-1/2 |
Tensile Elastic Modulus (23°C, 1mm/min) | 2700 | MPa | ISO 527-1/2 |
Flexural Maximum Load at 23°C (2 Mm/Min) | 90 | MPa | ISO 178 |
Flexural Modulus at 23°C | 2300 | MPa | ISO 178 |
Flexural Modulus (23°C, 2mm/min) | 2300 | MPa | ISO 178 |
Izod Impact Strength Unnotched at 23°C | N.B. | kJ/m2 | ISO 180/1U |
Izod Impact Strength Unnotched (23°C) | N.B. | kJ/m2 | ISO 180/1U |
Izod Impact Strength Notched at 23°C | 10 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (23°C) | 10 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched at -20°C | 6 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (-20°C) | 6 | kJ/m2 | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Density at 23°C | 1.11 | g/cm3 | ISO 1183 |
Density (23°C) | 1.11 | g/cm3 | ISO 1183 |
Moisture Absorption (23°C, 50% UR-HR) | 1.2 | % | ISO 62 |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 1.1 – 1.5 | % | Internal |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 1.1 - 1.5 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 1.1 – 1.5 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 1.1 - 1.5 | % | Internal |
Drying Temperature | 80 | °C | — |
Drying Time | 4 | h | — |
Melt Temperature | 260 - 290 | °C | — |
Mould Temperature | 60 - 80 | °C | — |
Value | Units | Test Method / Conditions | |
VICAT Softening Point (10 N - 50°C/h) | 255 | °C | ISO 306/A |
VICAT Softening Point (10N, 50°C/h) | 255 | °C | ISO 306/A |
VICAT Softening Point (50 N - 50°C/h) | 220 | °C | ISO 306/B |
VICAT Softening Point (50N, 50°C/h) | 220 | °C | ISO 306/B |
Heat Deflection Temperature (0,45 MPa - 120°C/h) | 180 | °C | ISO 75-1/-2 |
Heat Deflection Temperature (0.45 MPa, 120°C/h) | 180 | °C | ISO 75-1/-2 |
Heat Deflection Temperature (1,80 MPa - 120°C/h) | 75 | °C | ISO 75-1/-2 |
Heat Deflection Temperature (1.80 MPa, 120°C/h) | 75 | °C | ISO 75-1/-2 |
Value | Units | Test Method / Conditions | |
Hardness (thickness 1.6 mm) | 85 | Shore D | ISO 868 |
Rockwell Hardness | 115 | Scale R | ISO 2039-2 |
Hardness (thickness 1,6 mm) | 85 | Shore A | ISO 868 |
Burning Behaviour | HB | — | UL94 |