Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
Properties
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Other Properties
Value | Units | Test Method / Conditions | |
Tensile Stress at Break at 23°C | 90 | MPa | ISO 527-1/2 |
Tensile Stress at Break (23°C) | 90 | MPa | ISO 527-1/2 |
Tensile Strain at Break at 23°C | 4 | % | ISO 527-1/2 |
Tensile Strain at Break (23°C) | 4 | % | ISO 527-1/2 |
Tensile Elastic modulus 23°C (1 mm/min) | 7000 | MPa | ISO 527-1/2 |
Tensile Elastic Modulus (23°C, 1mm/min) | 7000 | MPa | ISO 527-1/2 |
Flexural Modulus (23°C) | 6000 | MPa | ISO 178 |
Flexural Modulus at 23°C | 6000 | MPa | ISO 178 |
Izod Impact Strength unnotched at 23°C (80 x 10 x 4.0 mm) | 10 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Unnotched (23°C, 80 x 10 x 4.0 mm) | 10 | kJ/m2 | ISO 180/1U |
Izod Impact Strength Notched at 23°C (80 x 10 x 4.0 mm) | 45 | kJ/m2 | ISO 180/1A |
Izod Impact Strength Notched (23°C, 80 x 10 x 4.0 mm) | 45 | kJ/m2 | ISO 180/1A |
Hardness Rockwell | 103 | Scale R | ISO 2039-2 |
Value | Units | Test Method / Conditions | |
Density at 23°C | 1,12 | g/cm3 | ISO 1183 |
Density (23°C) | 1.12 | g/cm3 | ISO 1183 |
Melt Volume Flow Rate - MVR at 190°C-2,16kg | 5 | cm3/10min | ISO 1133 |
Melt Flow Index (190°C, 2.16 kg) | 5 | cm3/10min | ISO 1133 |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 0,1 - 0,4 | % | Internal |
Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.1 - 0.4 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 0,4 - 0,6 | % | Internal |
Shrinkage - Normal (115mm x 50mm x 3mm) | 0.4 - 0.6 | % | Internal |
Melt Temperature | 200 - 240 | °C | — |
Mould Temperature | 50 -80 | °C | — |
Value | Units | Test Method / Conditions | |
VICAT Softening Point (50 N - 50°C/h) | 140 | °C | ISO 306/B |
VICAT Softening Point (50N, 50°C/h) | 140 | °C | ISO 306/B |
Heat Deflection Temperature (1,80 MPa - 120°C/h) | 145 | °C | ISO 75-1/-2 |
Heat Deflection Temperature (1.80 MPa, 120°C/h) | 145 | °C | ISO 75-1/-2 |
Value | Units | Test Method / Conditions | |
Burning Behaviour | HB | — | UL94 |
Regulatory & Compliance
- Certifications & Compliance