Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress at Break at 23°C 90 MPa ISO 527-1/2 Tensile Stress at Break (23°C, 5mm/min) 90 MPa ISO 527-1/2 Tensile Strain at Break at 23°C 4 % ISO 527-1/2 Tensile Strain at Break (23°C, 5mm/min) 4 % ISO 527-1/2 Tensile Elastic modulus 23°C (1 mm/min) 7000 MPa ISO 527-1/2 Tensile Elastic Modulus (23°C, 1mm/min) 7000 MPa ISO 527-1/2 Flexural Maximum Load at 23°C (2 Mm/Min) 130 MPa ISO 178 Flexural Modulus at 23°C 6000 MPa ISO 178 Flexural Modulus (23°C, 2mm/min) 6000 MPa ISO 178 Izod Impact Strength unnotched at 23°C (80 x 10 x 4.0 mm) 100 kJ/m2 ISO 180/1U Izod Impact Strength Unnotched (23°C, 80 x 10 x 4.0 mm) 100 kJ/m2 ISO 180/1U Izod Impact Strength Notched at 23°C (80 x 10 x 4.0 mm) 10 kJ/m2 ISO 180/1A Izod Impact Strength Notched (23°C, 80 x 10 x 4.0 mm) 10 kJ/m2 ISO 180/1A Izod Impact Strength Notched at 23°C (127x12.7x3.2 mm) 40 J/m ASTM D256 Izod Impact Strength Notched (23°C, 127x12.7x3.2 mm) 40 J/m ASTM D256 Hardness Rockwell 103 Scale R ISO 2039-2 - Typical Properties
Value Units Test Method / Conditions Density at 23°C 1,12 g/cm3 ISO 1183 Density (23°C) 1.12 g/cm3 ISO 1183 Melt Volume Flow Rate - MVR at 190°C-2,16kg 5 cm3/10min ISO 1133 Melt Flow Index (190°C, 2.16 kg) 5 cm3/10min ISO 1133 Shrinkage - Parallel (115mm x 50mm x 3mm) 0,1 - 0,4 % Internal Shrinkage - Parallel (115mm x 50mm x 3mm) 0.1 - 0.4 % Internal Shrinkage - Normal (115mm x 50mm x 3mm) 0,4 - 0,6 % Internal Shrinkage - Normal (115mm x 50mm x 3mm) 0.4 - 0.6 % Internal Melt Temperature 200 - 240 °C - Mould Temperature 50 -70 °C - - Thermal Properties
Value Units Test Method / Conditions VICAT Softening Point (50 N - 50°C/h) 140 °C ISO 306/B VICAT Softening Point (50N, 50°C/h) 140 °C ISO 306/B Heat Deflection Temperature (1,80 MPa - 120°C/h) 145 °C ISO 75-1/-2 Heat Deflection Temperature (1.80 MPa, 120°C/h) 145 °C ISO 75-1/-2 - Other Properties
Value Units Test Method / Conditions Burning Behaviour HB - UL94
Regulatory & Compliance
- Certifications & Compliance