Knowde Enhanced TDS
Identification & Functionality
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Additional Development Options
- Colors : xPP405-Black formula can be made in additional pigment colors. LCD
- Printers : xPP405-Black currently testing, there’s potential.
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Post Processing
xPP405-Black requires post processing to achieve specified properties. Prior to post curing, support structures should be removed from the printed part, and the part should be washed in a compatible cleaner. Nexa3D recommends either IPA or Cleaner C in 2 minute interval wash cycles. Use compressed air to remove residual solvent from the surface of the material between intervals.
- Post Curing
xPP405-Black requires post curing to achieve specified properties. A wide array of post cure equipment can be used to cure xPP405-Black appropriately.
- Limitations
Vat Printer : xPP405-Black formula is not possible.
Post Cure : xPP405-Black requires UV/Visible light post curing.
Properties
- Color
- Mechanical Properties
- Note
All specimen are printed unless otherwise noted. All specimen were conditioned in ambient lab conditions at 19-23C / 40-60% RH for at least 24 hours. ASTM Methods: D638 Type IV, 50mm/min, D790-B, 2mm/min, D256 Notched IZOD (Machine Notched), 6 mm x 12 mm, D648, D2240, Type “D” (0, 3 seconds), D1475, D7867
1) TaskID Reference: FOR16318
2) TaskID Reference: FOR16273
3) TaskID Reference: FOR5556
4) TaskID Reference: FOR9594
5) TaskID Reference: FOR16316
6) TaskID Reference: FOR16321
7) TaskID Reference: FOR10162
8) TaskID Reference: FOR16266
9) TaskID Reference: FOR16274
10) TaskID Reference: FOR18476
11) TaskID Reference: FOR16322
12) TaskID Reference: FOR17633
13) TaskID Reference: FOR18202
14) TaskID Reference: FOR18207
15) TaskID Reference: FOR18206
16) TaskID Reference: FOR16757
17) TaskID Reference: FOR21802
18) TaskID Reference: FOR18611
19) TaskID Reference: FOR18208
20) TaskID Reference: FOR18531
21) TaskID Reference: FOR19614
| Value | Units | Test Method / Conditions | |
| Tensile Stress at Break (Green)²¹ | 23 - 25 | MPa | ASTM D638 |
| Tensile Stress at Yield (Green)²¹ | 24 - 26 | MPa | ASTM D638 |
| Young’s Modulus (Green)²¹ | 877 - 917 | MPa | ASTM D638 |
| Elongation at Failure (Green)²¹ | 81 - 97 | % | ASTM D638 |
| Tensile Stress at Break (Post Processed)¹⁷ | 33 - 37 | MPa | ASTM D638 |
| Tensile Stress at Yield (Post Processed)¹⁷ | 37 - 39 | MPa | ASTM D638 |
| Young’s Modulus (Post Processed)¹⁷ | 1267 - 1333 | MPa | ASTM D638 |
| Elongation at Failure (Post Processed)¹⁷ | 88 - 112 | % | ASTM D638 |
| Maximum Flexural Stress(Post Processed)²⁰ | 44 - 46 | MPa | ASTM D790 |
| Flexural Modulus (Post Processed)²⁰ | 1235 - 1365 | MPa | ASTM D790 |
| Flexural Strain at Break (Post Processed)²⁰ | Does not break | — | ASTM D790 |
| Impact Strength - IZOD Notched (Post Processed)¹⁸ | 60 - 64 | J/m | ASTM D256 |
| Impact Strength - IZOD Unnotched (Post Processed)¹⁸ | min. 1500 | J/m | ASTM D256 |
| HDT (at 0.455 MPa, Post Processed)²² | 52.8 | °C | ASTM D648 |
| Hardness (0s, Post Processed)¹⁴ | 80 | Shore D | ASTM D2240 |
| Water Absorption (Post Processed)¹⁵ | 1 | % | Internal |
| Liquid Density (Post Processed)¹⁹ | 1.046 | — | ASTM D1475 |
| Solid Density (Green)¹⁹ | 1.116 | g/cm³ | ASTM D1475 |
| Solid Density (Post Processed)¹⁹ | 1.121 | — | ASTM D1475 |
| Viscosity (25°C, Post Processed)¹³ | 2410 | cP | ASTM D7867 |
| Hardness (3s, Post Processed)¹⁴ | 76 | Shore D | ASTM D2240 |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories