Next Polymers Next Nylon 6 Prime Series NX-01NC

Identification & Functionality

Chemical Family: Polyamides
Polymer Name: Polyamide 6 (PA 6)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Polyamides

Features & Benefits

Materials Features: Dimensional Stability,
Excellent Strength,
Good Mechanical Properties,
Good Stiffness,
Good Toughness,
High Durability,
High Elongation,
High Tensile Strength,
Semi Crystalline,
Weldable
Benefits: Non lubricated nylon6 .It exhibits good strength ,stiffness & Toughness.

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Consumer Goods,
Electrical & Electronics,
Industrial
Applications: Automotive & Transportation — Automotive
Electrical & Electronic Systems,
Exterior & Body,
Interior,
Other Automotive Applications
Building & Construction — Building Materials
Structural Components
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts,
Other Industrial Applications
Electrical & Electronics — Devices & Assemblies
Consumer Electronics
Consumer Goods — Furniture
Industrial — Leather & Textiles
Textile Manufacturing
Electrical & Electronics — Parts & Components
Connectors,
Housings & Enclosures,
Terminal Blocks, Plugs & Sockets
Plastics & Elastomers End Uses: Automotive Components,
Automotive Exterior Trim,
Automotive Interior Trim,
Bearings,
Bobbins,
Bushings,
Chair Bases,
Computer Components,
Connectors,
Fittings,
Housings,
Plugs
Plastics & Elastomers Processing Methods: Blow Molding,
Extrusion,
Injection Molding
Product Applications: Generally recommended for application such as wire devices ,plugs, receptacles , connectors ,convoluted tubing ,fillter housing,hings & Textiles components etc.
Processing Guide: Pre-Heating
The material is supplied in airtight 3 layer Paper +PE + Aluminum foil liner bags, Still Nylon being hygroscopic material it is recommended for hot air drying at 80 °C for 4 to 6 Hrs ensuring maximum water content as 0.2 %.
Post Molding Recommendations: Molded components should be conditioned in water at a min of 95 deg C until they absorb 0.8-1.2 % of water above their original weight.

Properties

Color: Natural
Flame Rating: UL 94 HB
Mechanical Properties
Thermal Properties
Electrical Properties
Other Properties
Injection Molding
Rheological Properties

	Value	Units	Test Method / Conditions
Tensile Strength	75.0	MPa	ASTM D-638
Elongation at Break	min. 50	%	ASTM D-638
Flexural Strength	96.0	MPa	ASTM D-790
Flexural Modulus	2900.0	MPa	ASTM D-790
Izod Notched Impact Strength(23°C)	5.0	Kg-cm/cm	ASTM D-256 A
Rockwell Hardness	95.0	R Scale	ASTM D-785
Rockwell Hardness	80.0	M Scale	ASTM D-785

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (18.5Kg/Sq Cm Load)	65.0	°C	ASTM D-648
Heat Deflection Temperature (4.5Kg/Sq Cm Load)	178.0	°C	ASTM D-648
Melting Point	220.0	°C	ASTM D-2117
Flammability UL 94(Thickness 0.8mm)	H.B.	—	ISO1210/UL-94

	Value	Units	Test Method / Conditions
Dielectric Strength	32.0	KV / mm	IEC 60243
Comparative Tracking Index	600.0	—	IEC60112
Volume Resistivity	10000000000000.0	Ohms – m	IEC 60093
Surface Resistivity	100000000000000.0	Ohms	IEC 60093

	Value	Units	Test Method / Conditions
Specific Gravity	1.13	—	ASTM D-792
Water Absorption(Saturation. immersed)	9.5	%	ASTM D-570
Water Absorption (23°C , 24 Hrs)	1.6	%	ASTM D-570

	Value	Units	Test Method / Conditions
Feed Zone	230 - 240	°C	—
Compression Zone	240 - 260	°C	—
Mixing Zone	260 - 270	°C	—
Mould Temperatures	80 - 95	°C	—

	Value	Units	Test Method / Conditions
Mold Shrinkage(Parallel)	1.28	%	ASTMD-955
Mold Shrinkage(Normal)	1.28	%	ASTMD-955

Regulatory & Compliance

Certifications & Compliance: UL 94
Regulations compliance: Directive 1907/2006/EC This grade complies with ROHS directive 2002/95/EC Unless specified, this grade is not suitable for food contact, medical devices or toy applications