Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
- Benefits
Good combination between Mechanical and electrical properties .exceptional degree of inherent thermal stability ,chemical resistance & flame resistance.
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Product Applications
High Performance plactic materials that are used a wide spectrum of application Appliance,Automotive,Electric/Electronics,industrial & medical Technology etc.
- Processing Guide
Pre-Heating
The material is supplied in airtight 3 layer Paper +PE + Aluminum foil liner bags, it is recommended for hot air drying at 130 °C for 4 to 6 Hrs ensuring maximum water content as 0.1 %.- Post Molding Recommendations
A mold temperature largely determine the crystallanity of PPS .& thus effects the parts final physical properties and appreances .so rapidely that a hot mold will produce dimensially stable parts able to resist dimensional changes even at eleveted temerature.
Properties
- Color
- Flame Rating
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Other Properties
- Injection Molding
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 110.0 | MPa | ASTM D-638 |
| Tensile Modulus | 18000.0 | MPa | ASTM D-638 |
| Elongation at Break | 1.5 | % | ASTM D-638 |
| Flexural Strength | 205.0 | MPa | ASTM D-790 |
| Flexural Modulus | 17500.0 | MPa | ASTM D-790 |
| Izod Notched Impact Strength(23°C) | 9.0 | Kg-cm/cm | ASTM D-256 A |
| Rockwell Hardness | 110.0 | R Scale | ASTM D-785 |
| Rockwell Hardness | 100.0 | M Scale | ASTM D-785 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (18.5Kg/Sq Cm Load) | 270.0 | °C | ASTM D-648 |
| Heat Deflection Temperature (4.5Kg/Sq Cm Load) | 280.0 | °C | ASTM D-648 |
| Melting Point | 285.0 | °C | ASTM D-2117 |
| Flammability UL 94(Thickness 0.8mm) | V0 | - | ISO1210/UL-94 |
| UL,RTI Mechanical ,With impact | 240.0 | - | UL-746B |
| UL RTI Electrical | 220.0 | - | UL-746B |
| Value | Units | Test Method / Conditions | |
| Dielectric Strength | 22.0 | - | ASTMD-149 |
| Relative Permittivity (60 Hz) | 225.0 | KV/mm | ASTMD-150 |
| Volume Restivity | 100000000000000.0 | Ohms –cm | IEC60243 |
| Surface Restivity | 1.0e+15 | Ohms | IEC 60093 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.95 | - | ASTM D-792 |
| Filler Content | 65.0 | % | ASTMD-5630 |
| Water Absorption(Saturation. immersed) | 4.2 | % | ASTM D-570 |
| Water Absorption (23°C , 24 Hrs) | 0.02 | % | ASTM D-570 |
| Value | Units | Test Method / Conditions | |
| Feed Zone | 290 - 300 | °C | - |
| Compression Zone | 310 - 320 | °C | - |
| Mixing Zone | 320 - 330 | °C | - |
| Mould Temperatures | 135 - 149 | °C | - |
| Value | Units | Test Method / Conditions | |
| Mold Shrinkage(Parallel) | 0.2 | % | ASTMD-955 |
| Mold Shrinkage(Normal) | 0.2 | % | ASTMD-955 |
Regulatory & Compliance
- Certifications & Compliance
- Regulations compliance
Directive 1907/2006/EC This grade complies with ROHS directive 2002/95/EC.