Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- IEC 60695-11-10 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Other Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus | 9800 | MPa | ISO 527 |
Yield stress | 185 | MPa | ISO 527 |
Strain at break | 2.5 | % | ISO 527 |
Flexural Modulus | 5500 | MPa | ASTM D 790 |
Flexural modulus, 23° | 8500 | MPa | ISO 178 |
Charpy notched impact strength (+23°) | 12 | kJ/m2 | ISO 179/1eA |
Charpy impact strength (-30°) | 41 | kJ/m2 | ISO 179/1eU |
Charpy impact strength (+23°) | 53 | kJ/m2 | ISO 179/1eU |
Charpy notched impact strength (-30°) | 9.5 | kJ/m2 | ISO 179/1eA |
Izod notched impact strength | 8 | kJ/m2 | ISO 180/1A |
Izod notched impact strength, +23° | 10 | kJ/m2 | ISO 180/1A |
Temperature | -30 | °C | — |
Flexural modulus temperature | 90 | °C | — |
Value | Units | Test Method / Conditions | |
Molding shrinkage - normal | 0.8 | % | ISO 294-4, 2577 |
Molding shrinkage - parallel | 0.4 | % | ISO 294-4, 2577 |
Density | 1370 | kg/m3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Temperature of deflection under load (1.80 Mpa) | 250 | °C | ISO 75-1/-2 |
Temperature of deflection under load (0.45 Mpa) | 260 | °C | ISO 75-1/-2 |
Oxygen index | 26 | % | ISO 4589-1/-2 |
Thickness tested | 0.8 | mm | — |
Vicat softening temperature | 250 | °C | ISO 306 |
Burning Behavior at 1.5 mm nominal thickness | HB | class | IEC 60695-11-10 |
Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Yellow Card available | yes | - | — |
Value | Units | Test Method / Conditions | |
Water absorption | 5.5 | % | Sim. to ISO 62 |