Value | Units | Test Method / Conditions | |
Tensile Strength | 510 | ksi | — |
Tensile Strength | 360 | kgf/mm2 | — |
Tensile Strength | 3530 | MPa | — |
Tensile Strength | 510.0 | ksi | — |
Tensile Strength | 360.0 | kgf/mm2 | — |
Tensile Strength | 3530.0 | MPa | — |
Tensile Modulus | 134 | msi | — |
Tensile Modulus | 94 | 103kgf/mm2 | — |
Tensile Modulus | 920 | GPa | — |
Tensile Modulus | 134.0 | msi | — |
Tensile Modulus | 94.0 | 103kgf/mm2 | — |
Tensile Modulus | 920.0 | GPa | — |
Ultimate Elongation | 0.3 | % | — |
Density | 2.19 | g/cm3 | — |
Filament Diameter | 7 | µm | — |
Filament Diameter | 7.0 | µm | — |
Filaments per Yarn | 1500/3000/6000 | — | — |
Yield | 125/250/520 | g/km | — |
CTE | -1.5 | 10-6/K | — |
Thermal Conductivity | 600 | W/m・K | — |
Thermal Conductivity | 600.0 | W/m・K | — |
Electrical Resistivity | 2.2 | 10-4 Ω⋅ cm | — |
Value | Units | Test Method / Conditions | |
0 deg Tensile Strength | 1900 | MPa | — |
0 deg Tensile Strength | 1900.0 | MPa | — |
0 deg Tensile Modulus | 540 | GPa | — |
0 deg Tensile Modulus | 540.0 | GPa | — |
Elongation | 0.3 | % | — |
0 deg Compressive Strength | 340 | MPa | — |
0 deg Compressive Strength | 340.0 | MPa | — |
0 deg Compressive Modulus | 540 | GPa | — |
0 deg Compressive Modulus | 540.0 | GPa | — |
90 deg Tensile Strength | 25 | MPa | — |
90 deg Tensile Strength | 25.0 | MPa | — |
90 deg Tensile Modulus | 5.5 | GPa | — |
Short beam shear Strength | 60 | MPa | — |
Short beam shear Strength | 60.0 | MPa | — |