- Appearance
- Colorless, Black
- Typical Properties
- Notes
Standard Curing Condition 60℃-2hour or 80℃-1hour
Curing Condition:60℃×2hrs+25℃×48hrs
※Curing Condition:80℃×1hr+25℃×192hrs
The above values are typical and not specification
Value | Units | Test Method / Conditions | |
Specific Gravity (25°C) | 0.92 | — | — |
Viscosity (25°C) | 900.0 | mPa.s | — |
Mixing Ratio (parts by weight) | 100/30 | — | — |
Gel Time (60°C) (25g) | 40~45 | mPa・s | — |
Pot Life (25°C, time up to 10Pa.s) | 60.0 | mPa.s | — |
Pot Life (40°C、time up to 10Pa.s) | 45.0 | minute | — |
Mixed Viscosity (25°C) | 700.0 | min | — |
Mixed Viscosity (40°C) | 350.0 | min | — |
Hardness (25°C) | 30.0 | Shore A | JIS K 7215 |
Specific Gravity | 1.0 | g/cm3 | JIS C 2105 |
Glass Transition Temperature (TMA) | -70.0 | °C | — |
Coefficient of Thermal Expansion above Tg | 18.5×10-5 | °C | — |
Coefficient of Thermal Expansion below Tg | 6.61×10-5 | °C | — |
Tensile Strength (25°C dumbbell No.) | 2.6 | MPa | JIS K 7312 |
Elongation (25°C dumbbell No.) | 300.0 | % | JIS K 7312 |
Young's Modulus (25°C dumbbell No.2) | 0.66 | MPa | JIS K 7312 |
Tear Strength (25°C) | 8.2 | N/mm | JIS K 7312 |
Shear Adhesive Strength (-40°C) | 12.2 | MPa | JIS K 6850 |
Shear Adhesive Strength (25°C) | 2.1 | MPa | JIS K 6850 |
Shear Adhesive Strength (150°C) | 0.6 | MPa | JIS K 6850 |
Volume Resistivity (25°C) | 3.3×1015 | Ω・cm | JIS K 6911 |
Volume Resistivity (25°C boil for 2hrs) | 3.4×1014 | Ω・cm | JIS K 6911 |
Dielectric constant (1kHz 100kHz 1MHz) | 4.6 3.7 3.3 | — | JIS K 6911 |
Dielectric Tangent (1kHz 100kHz 1MHz) | 6.8 7.6 7.1 | % | JIS K 6911 |
Water Absorption (boil for 2hrs) | 0.52 | wt% | JIS K 6911 |
Water Absorption (boil for 2hrs) | 0.68※ | wt% | JIS K 6911 |
Shrinkage | 0.6 | % | ASTM D2566-68 |
Breakdown Voltage (23°C 50%RH) | 23.6 | kV/mm | ASTM D149 |