Standard Curing Condition 60℃-3hour
Value | Units | Test Method / Conditions | |
Specific Gravity (25°C) | 1.21 | — | — |
Viscosity (25°C) | 200.0 | mPa.s | — |
Mixing Ratio (25°C) | 60.0 | — | — |
Mixed Viscosity (25°C) | 100/33 | mPa.s | — |
Mixed Specific Gravity (60°C) | 600.0 | - | — |
Gel Time Parts by Weight | 1.0 | min | — |
Pot Time (25°C, time up to 10Pa.s) | 45.0 | minute | — |
Hardness (25°C) | 24.0 | Shore A | JIS K 7215 |
Glass Transition Temperature (TMA) | 21.0 | °C | — |
Coefficient of Thermal Expansion above Tg | 23×10-5 | °C | — |
Tensile Strength (25°C dumbbell No.2) | 1.1 | MPa | JIS K 7312 |
Elongation (25°C dumbbell No.2) | 180.0 | % | JIS K 7312 |
Tear Strength (25°C) | 4.1 | N/mm | JIS K 7312 |
Volume Resistivity (25°C) | 19.8 9.9 5.8 | Ω・cm | JIS K 6911 |
Dielectric constant (1kHz 100kHz 1MHz) | 0.2 | — | JIS K 6911 |
Dielectric Tangent (1kHz 100kHz 1MHz) | Equivalent V-2 | % | JIS K 6911 |
Water Absorption (boil for 1hr) | 5.6×1013 | wt% | JIS K 6911 |
Flame Resistance | 5.8 3.6 3.2 | - | UL94 |