Properties
- Appearance
- Black
- Typical Properties
- Notes
Standard Curing Condition 60℃-2hour or 80℃-1hour
Value | Units | Test Method / Conditions | |
Specific Gravity (25°C) | 2.52 | — | — |
Viscosity (25°C) (40°C) | 18250.0 | mPa.s | — |
Mixing Ratio (parts by weight) | 100/6 | — | — |
Pot Time | 10.0 | minute | — |
Gel Time | 7~8 | min | — |
Mixed Viscosity (25°C 256g,2min) | 22000.0 | mPa.s | — |
Mixed Viscosity (A:50°C, B:25°C) | 12000.0 | mPa.s | — |
Appearance 25°C | 80.0 | shore A | JIS K 7215 |
Hardness (25°C) | 2.42 | — | JIS K 7112 |
Tensile Strength (25°C) | 4.3 | MPa | JIS K 7312 |
Elongation (25°C) | 42.0 | % | JIS K 7312 |
Glass Transition Temperature (TMA) | -46.3 | °C | — |
Shear Adhesive Strength (25°C) | 2.07 (ABS) | °C | JIS K 6850 |
Volume Resistivity (25°C) | 5.7×1014 | °C | JIS K 6911 |
Water Absorption (boil/2hrs,2mmt) | 0.39 | MPa | — |
Dielectric constant (1kHz 100kHz 1MHz) | 7.7, 6.5, 6.1 | Ω・cm | JIS K 6911 |
Dielectric Tangent (1kHz 100kHz 1MHz) | 5.5, 5.1, 4.3 | % | JIS K 6911 |
Thermal Conductivity (300g) | 1.8 | — | — |
Flame Resistance (1/8 inch) | Equivalent V-2 | % | UL-94 |
Coefficient ofThermal Expansion above Tg | 8.8×10-5 | W/mK | — |
Coefficient ofThermal Expansion below Tg | 4.2×10-5 | 2mmt | — |