Features & Benefits
- Ready-to-Use Product Features
- Feature
- Offers excellent adhesion for Metal plate, plastic plate (PP, PE, etc.), rubber plate, foam by using the special rubber adhesive.
- Offers superior repulsion property.
- VR-5000T is good performance for rough surface because of its thickness.
- Ten restricted substances by RoHS2 are not contained.
Applications & Uses
- Markets
- Compatible Substrates & Surfaces
- Application
- Bonding of metals plates, plastic plates, rubbers and foams.
- Bonding of parts in: Printers, Copiers, Televisions, Other office equipment and Home appliances
- Fixing parts of digital camera - High adhesion to rubber
- Fixing brash of vacum cleaner - High adhesion without primer
- Fixing parts of toner cartridges - High repulsion resistance
- Usage Precautions
- Remove all oil, moisture and dirt from the surface of the substrate before applying.
- Since the tape is pressure-sensitive adhesive, be sure to apply enough pressure with a roller or press when applying. Otherwise it might be affected to its properties and appearance.
- The tape may not adhere well to extremely uneven or distorted surfaces. Enough Leveling off the surface should be required before applying.
- It takes certain time to get full adhesive strength after applying, keep away the tape from any stress for a several hours after applying.
- Depending on a rubber material, there may be a risk of affecting adhesive property over time due to migration of component from rubber material. Please conduct a thorough evaluation in advance, on initial adhesive strength and its change over time.
- This product uses a rubber adhesive, which is easily affected by heat and oxygen compared to acrylic adhesive. Please conduct a thorough evaluation in advance on initial adhesive properties and its change over time, to determine application area and usage.
Properties
- Typical Properties
- Properties
180 degree peeling adhesion for each substrate
Substrate VR-5000T Stainless steel plate 50 Aluminum plate 47 Glass plate 50 ABS plate 40 PCABS plate 42 Polystyrene plate 50 HIPS plate 50 Polycarbonate plate 50 Polypropylene plate 40 POM plate 40 Polyethylene plate 33 EPT rubber 25 
(Unit：N/20mm)
Tape size ：20mm width
Backing material ：PET#50
Pressing condition ：1 pass back and forth with a 2 kg roller at 23 degree C, 50% RH
Applying condition ：23 degree C/50%RH × 30min
Peeling speed ：300mm/min
Peeling angle ：180 degree
Measurement temp ：23 degree C, 50%RH
180 degree peeling adhesive strength for each temperature
Temperature VR-5000T 0 degree C 47 23 degree C 50 40 degree C 48 60 degree C 40
(Unit: N/20mm)
Substrate ：Stainless steel plate
Tape size ：20mm width
Backing material ：PET#50
Pressing condition ： 1 pass back and forth with a 2 kg roller
Bonding temperature ：23degreeC/50%RH
Curing condition ：Measurement temperature x 30 min
Peeling speed ：300 mm/min
Peeling angle ：180 degree
Measurement temperature：0, 23, 40, 60 degree C
180 degree peeling strength - Aging after application
Aging after application VR-5000T 1 min later 45 30 min (Initial) later 50 24 hours later 53 48 hours later 55 72 hours later 55 168 hours later 55
(Unit: N/20mm)
Substrate ：Stainless steel plate
Tape size ：20mm width
Backing material ：PET#50
Pressing condition ：1 pass back and forth with a 2 kg roller
Bonding temperature: 23degreeC/50%RH
Curing condition ：23degreeC/50%RHx 1min, 30min, 24hr, 48hrs, 72hrs, 168hrs
Peeling speed ：300 mm/min
Peeling angle ：180 degree
Measurement temperature：23degreeC/50%RH180° peeling strength for each application pressure
Application VR-5000T 0.1 kg roller 35 0.5 kg roller 46 2 kg roller 50 5 kg roller 52
(Unit: N/20mm)
Substrate ：Stainless steel plate
Tape size ：20mm width
Backing material ：PET#50
Pressing condition ： 1 pass back and forth with a 0.1 kg, 0.5 kg, 2 kg, 5 kg roller,
Bonding temperature ：23degreeC/50%RH
Curing condition ：23degreeC/50%RH x 30 min
Peeling speed ：300 mm/min
Peeling angle ：180degree
Measurement temperature：23degreeC/50%RH
Shearing adhesive strength for each substrate
Substrate VR-5000T Stainless steel plate 350 Aluminum plate 470 ABS plate 350 Polystyrene plate 350 Polycarbonate plate 380 
(Unit：N/20mm×20mm)
Tape area ：20mm×20mm
Pressing condition ：1 pass back and forth with 5 kg at 23 degree C/50%RH
Applying condition ：23 degree C/50%RH×30min
Peeling speed ：50mm/min
Measurement temp ：23 degree C/50%RH
Holding power
Temperature VR-5000 23 degree C 0.1 40 degree C 0.2 60 degree C 0.2 
(Unit：mm/hr)
Substrate ：Phenol resin plate
Backing material ：PET#25
Pressing condition ：1 pass back and forth with 2 kg at 23 degree C/50%RH
Applying condition ：23 degree C/50%RH×30min
Tape area ：20mm×10mm
Load ：4.9N(500gf)
Load time ：1h
Static load peeling
Substrate VR-5000T Stainless steel plate 0.8 ABS plate 0.8 Polystyrene plate 1 Polypropylene plate 0.8 
(Unit：mm)
Tape area ：10mm×50mm
Backing material ：PET#25
Pressing condition ：1 pass back and forth with a 2 kg roller at 23 degree C/50%RH
Applying condition ：23 degree C/50%RH×30min
Load ：0.98N(100gf)
Application temp ：23 degree C/50%RH
Load time ：24hrs
Resistance to repulsion for plastic plate
Substrate VR-5000T ABS plate <1 Polypropylene plate <1 Polystyrene plate <1 
(Unit：mm)
Tape area ：20mm×180mm
Substrate size ：30mm×200mm
Backing material ：AL（t=0.5mm）
Pressing condition ：23 degree C/50%RH
Applying condition ：23 degree C/50%RH for 24 hrs
Repulsion condition： Laminate a substrate and AL plate with tape by laminating machine. Fit the left sample into wooden mold then leave it at 70 degree C x 72 hrs and measure the floating height.
180 degree peeling adhesion -Aging(durability) at each condition after applying
Condition VR-5000T Initial(23 degree C/50%RH×30min) 50 －30 degree C×30 days 60 80 degree C
14 days 65 30 days 65 40 degree C/92%RH×30 days 66 60 degree C/95%RH×30 days 67 Heat shock[100cycle] *1 65 Heat cycle[40cycle]*2 64 *1：Heat shock condition [-40 degree C × 30min⇔90 degree C × 30min] 100cycle
*2：Heat cycle condition [-20 degree C × 6hr ⇒ (1hr) ⇒ 60 degree C/95%RH × 6hr ⇒ (1hr) ⇒] 40cycle(Unit：N/20mm)
Substrate ：Stainless plate
Tape size ：20mm width
Backing material ：PET#50
Pressing condition ：1 pass back and forthwith 2 kg roller at 23 degree C/50%RH
Applying condition ：Refer to the left table
Peeling speed ：300mm/min
Peeling angle ：180 degree
Measurement temperature ：23 degree C/50%RH
| Value | Units | Test Method / Conditions | |
| Thickness | 0.3 | mm | - |
| 180° Peeling Force | 50.0 | N/20mm | - |
Safety & Health
- Safety Precaution
- Take a careful consideration if this product is adapted to the use, purpose and condition before using. The tape may peel in some cases depending on substrate and attachment conditions.
- When using this product in areas that may pose a risk of accident, use together with a different joining method.
Packaging & Availability
- Sizes
Tape thickness(mm) Width(mm) Length(M) 0.30 5 - 1050 50
Storage & Handling
- Storage Precautions
- Make sure to store this product in a box.
- Avoid storing in high-temperature or high-moisture areas. This product should be stored in a cool, dark area away from direct sunlight.
- Please use this tape within 6 months of storage.