Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Basis
- Neutral Oxime Silicone
- Consistency
- Non-Slump Paste
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Benefits
- Wood color appearance.
- Low modulus and high elasticity.
- Excellent adhesion to a wide range of substrates without priming.
- UV radiation, weather and aging resistant
- Extremely long service life.
- Low odor.
- Non-corrosive.
Applications & Uses
- Markets
- Application Method
- Cure Method
- Fields of Applications
- Suitable as a joint sealant on porous and non-porous substrates including concrete, masonry, brick, aluminum, PVC, glass, ceramics and most plastics.
- Provide a color matched seal between walls and imitation wood window/ door frames.
- Sealing of joints between wooden floors and walls.
- Perimeter and connection joints in aluminum, wood and PVC carpentry.
- Direction for Use
Surface preparation and sealant application:
Cleaning and joint preparation:
Substrates joint flanks) must be clean, dry, and free of dust, grease and other contaminant which may affect the adhesion. Non
porous surfaces (such as aluminum, glass, etc.) should be cleaned with a suitable solvent and thoroughly dried with a clean cloth.
Porous substrates (such as concrete, brickwork, etc.) must be mechanically cleaned from loose particles. Mask off the joint edges.
Primer
OLIVE C-25m adheres to most common construction materials without primer. However, a preliminary adhesion test is recommended
on every surface. Sometimes, it may be necessary to treat the joint surfaces with a primer to obtain better adhesion performances.
Product Application Olive PRIMER 10 Porous surfaces. (e.g. concrete, cement, marble, natural and artificial stone, etc.)Olive PRIMER 20: Non-porous surfaces. (e.g. aluminum, iron, stainless steel, zinc, copper, brass, painted surfaces and most plastics)Olive PRIMER 80DS: All surfaces. Substrates exceptionally difficult to adhere on.
Inserting backing material
Use the closed cell polyethylene backer foam OLIVE CORDON CELULAR as a back-up material to limit the sealant joint depth and avoid the sealant to adhere to the joit base. Choose the right backing strip diameter (at least 25% wider than the joint width).
Silicone sealant application
After substrate preparation, apply the sealant with a professional caulking gun, evenly and without bubbles. Observe the eventually used primer's open time before filling the joint.Remarks
Do not use OLIVE C-25m on bituminous substrates or on building materials which might bleed oils, plasticizers or solvents. (e.g. natural rubber, chloroprene, EPDM).
There is no adhesion to PE, PP, PTFE (Teflon®). Due to the wide variety of possible substrates, we recommend a preliminary compatibility test.
OLIVE C-25m cannot be overpainted.
Not intended for structural glazing.- Joint Design
Expansion joints should be correctly dimensioned taking account of dimensional changes in the substrates due to thermal filuctuations. Joint's dimensions should match with the sealant movement capability, with a maximum permitted value of 25%
Use closed cell polyethylene backer foam (Olive Backer Rod) as a back-up material to
limit the sealant joint depth and avoid three-sided adhesion.
The following general rules/recommendations should be followedGeneral statement: The ideal joint has a 2:1 width: depth ratio
Minimum joint dimensions 5-6mm width x 5-6 mm depth.
Up to 12 mm wide: Width = depth From 12mm to 24mm wide Depth = ½ width Wider than 24mm Depth = 12-15mm
Expansion joints should not be wider than 50mm 
Properties
- Physical Form
- Physical Properties
- Mechanical Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Specific Gravity | approx. 1.24 | g/ml | ISO 2811-1 |
| Value | Units | Test Method / Conditions | |
| Hardness | approx. 26 | Shore A | ISO 7619-1 |
| Tensile Modulus of Elasticity (100%, 2 mm thickness, S2 dumbbells, 7 days, 23°C: 50% R.H.) | 0.5 | Mpa | ISO 37 |
| Tensile Strength (2 mm thickness, S2 dumbbells, 7 days, 23°C: 50% R.H.) | 1.3 | Mpa | ISO 37 |
| Tensile Elongation at Break (2 mm thickness, S2 dumbbells, 7 days, 23°C: 50% R.H.) | 550.0 | % | ISO 37 |
| Tensile Modulus of Elasticity (100%, 12x12x50 mm joint, 28 days, 23°C: 50% H.R.) | 0.55 | Mpa | ISO 8339 |
| Tensile Strength (12x12x50 mm joint, 28 days, 23°C: 50% H.R.) | 0.65 | Mpa | ISO 8339 |
| Tensile Elongation at Break (12x12x50 mm joint, 28 days, 23°C: 50% H.R.) | 225.0 | % | ISO 8339 |
| Value | Units | Test Method / Conditions | |
| Tack Free Time (23ºC: 50% R.H.) | approx.5 | minutes | OQ.06-internal |
| Skin Forming Time (23°C, 50% R.H.) | approx. 10 | Minutes | OQ.16-internal |
| Curing Rate | approx. 3 | mm/24 h | OQ.18-internal |
| Resistance to Flow (5ºC and 50ºC) | 0.0 | mm | ISO 7390 |
| Loss of Volume (60% Elongation) | min. 85 | % | ISO 10563 |
| Elastic Recovery | 12.5 | % | ISO 7389 |
| Movement Capability | max. 25 | % | ISO 11600 |
| Total VOC Content | approx. 115 | g/l | SCAQMD rule 1168 |
| Application Temperature | 5-40 | ºC | — |
| Service Temperature | -40 to +150 | ºC | — |
Regulatory & Compliance
- Environmental Regulations
- French VOC-emission class A+.
- Conforms to LEED® IEQ-credits 4.1 (Indoor Environmental Quality) adhesives and sealants.
- Product Certifications
Olive C-25m meets the following specifications
- ISO 11600-F 12,5E.
- CE marking: EN 15651-1 F-EXT-INT-CC
- EN 15651-2 G-CC
Safety & Health
- Safety
Use in well-ventilated areas, avoiding contact with skin and eyes. Keep out of the reach of children. Information relating to the safety of the product is available on the safety data sheet (SDS) Before using the product, we advise you to carefully read the SDS and the safety labels.
Packaging & Availability
- Packaging Type
- Packaging Information
This product is available in 300ml cartridges and 600ml sausages. Other packaging is available under request.
Storage & Handling
- Storage
The shelf life is 12 months in its unopened original packaging, in dry conditions and protected from direct sunlight at temperatures between +5ºC and +25ºC.