Parts by weight:
Ocpol 701 100 Catalyst K 10 2ml - Applications
- To start the curing reaction, take 100 parts of resin.
- Catalyst K 10 should be added to the resin system shortly before application to initiate the polymerization reaction.
- It is important to add the catalyst in carefully measured amounts to control the polymerization. Too much catalyst will cause too rapid a gelation time, whereas too little catalyst will result in under cure.
- Care must be taken to avoid explosive violence. Do not mix catalyst and cobalt octate or any accelerator together.
Properties
- Physical Form
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Viscosity at 25°C | 300 - 400 | cps | Brookfield LVT sp. 3@60 rpm |
| Gel Time at 25°C | 10 – 15 | min | — |
| Gel Time at 25°C - 35°C | 14 – 24 | — | — |
| Gel Time at 25°C – Peak | max. 40 | — | — |
| Acid value | max. 26 | mg KOH/g | — |
| Solid content | 58±2 | % | — |
| Specific Gravity at 25°C | 1.10 – 1.11 | — | — |
| Peak Temperature | min. 170 | — | — |
| Barcol hardness (Model GYZJ 934 – 1) | 43 - 47 | — | — |
| Heat deflection temperature | 70 - 75 | °C | — |
| Water absorption 24 h at 23°C | 15 - 18 | mg | — |
| Elongation at break at 20°C | 1.9 – 2.2 | % | — |
| Tensile strength | 70 - 75 | Mpa | — |
| Flexural strength | 3500 - 3750 | Mpa | — |
| Tensile modulus | 120 - 130 | Mpa | — |
| Flexural Strength | 3600 - 3800 | Mpa | — |
Safety & Health
- Safety
Due attention should be given to the precautions for handling chemicals provided in our Material Safety Data Sheet.