Parts by weight:
Ocpol 710 100 Cobalt 1% 1.5ml Catalyst K 10 1.5ml - Applications
- To start the curing reaction, take 100 parts of resin.
- Catalyst K 10 should be added to the resin system shortly before application to initiate the polymerization reaction.
- It is important to add the catalyst in carefully measured amounts to control the polymerization. Too much catalyst will cause too rapid a gelation time, whereas too little catalyst will result in under cure.
- Care must be taken to avoid explosive violence. Do not mix catalyst and cobalt octate or any accelerator together.
Properties
- Physical Form
- Appearance
- Cloudy
- Typical Properties
Value | Units | Test Method / Conditions | |
Viscosity at 25°C | 400 - 500 | cps | Brookfield LVT sp. 3@60 rpm |
Gel Time at 25°C | 10 – 15 | min | — |
Acid value | max. 26 | mg KOH/g | — |
Solid content | 58±1 | % | — |
Specific Gravity at 25°C | 1.11 – 1.13 | — | — |
Peak Temperature | min. 170 | — | — |
Barcol hardness (Model GYZJ 934 – 1) | 43 - 47 | — | — |
Heat deflection temperature | 63 - 71 | °C | — |
Water absorption 24 h at 23°C | 16 - 19 | mg | — |
Elongation at break at 20°C | 1.9 – 2.2 | % | — |
Tensile strength | 55 – 65 | Mpa | — |
Tensile modulus | 3600 - 3800 | Mpa | — |
Flexural Strength | 182 - 195 | Mpa | — |
Safety & Health
- Safety
Due attention should be given to the precautions for handling chemicals provided in our Material Safety Data Sheet.
Packaging & Availability
- Packaging Type
- Packing
Ocpol 710 is supplied in 220 Kg new steel drums with close top.